<abstract xmlns="http://www.w3.org/1999/xhtml">

<p>The correct manufacture of products using FDM printers is not an easy task, taking into account the value and repeatability of material properties. The properties of elements manufactured in this way depend on many factors, both technological and material. Poly(lactic acid) PLA is one of the most willingly used materials in additive techniques. It is sold in a very wide range of colours. This work was intended to answer the question of how the type of pigment affects the mechanical and thermal properties of products obtained from PLA. The correlation between the material properties and the structure of the material as well as the macroscopic structure of the product has also been investigated. The paper analyses the mechanical and thermal properties of products made of PLA filaments in 12 basic colours obtained from one supplier. Bending, impact strength, HDT and Vicat softening point tests were carried out. The percentage content of residues after calcination the samples was determined. Additional analysis (DSC) was performed to interpret the obtained tests results. They indicate that the mechanical properties differ significantly between different types of PLA with differences of up to 45%. Vicat softening point tests indicate differences of 5°C between the extreme values of these parameters. The DSC interpretive study did not clearly show the reasons for these differences in the properties of the filaments.</p>
</abstract>

The correct manufacture of products using FDM printers is not an easy task, taking into account the value and repeatability of material properties. The properties of elements manufactured in this way depend on many factors, both technological and material. Poly(lactic acid) PLA is one of the most willingly used materials in additive techniques. It is sold in a very wide range of colours. This work was intended to answer the question of how the type of pigment affects the mechanical and thermal properties of products obtained from PLA. The correlation between the material properties and the structure of the material as well as the macroscopic structure of the product has also been investigated. The paper analyses the mechanical and thermal properties of products made of PLA filaments in 12 basic colours obtained from one supplier. Bending, impact strength, HDT and Vicat softening point tests were carried out. The percentage content of residues after calcination the samples was determined. Additional analysis (DSC) was performed to interpret the obtained tests results. They indicate that the mechanical properties differ significantly between different types of PLA with differences of up to 45%. Vicat softening point tests indicate differences of 5°C between the extreme values of these parameters. The DSC interpretive study did not clearly show the reasons for these differences in the properties of the filaments.

PLA filament is not equal to PLA filament: Experimental studies of the influence of the type of pigment on the mechanical and thermal properties of poly(lactic acid) products

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

The correct manufacture of products using FDM printers is not an easy task, taking into account the value and repeatability of material properties. The...

PLA filament is not equal to PLA filament: Experimental studies of the influence of the type of pigment on the mechanical and thermal properties of poly(lactic acid) products

Published Online: Aug 25, 2023

Page range: 177 - 190

Received: Mar 22, 2023

Accepted: Jun 25, 2023

DOI: https://doi.org/10.2478/msp-2023-0015

Keywords
PLA, pigments, mechanical properties, DSC, colours, thermal properties

© 2023 Jacek Iwko et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

PLA filament is not equal to PLA filament: Experimental studies of the influence of the type of pigment on the mechanical and thermal properties of poly(lactic acid) products

Published Online: Aug 25, 2023

Page range: 177 - 190

Received: Mar 22, 2023

Accepted: Jun 25, 2023

DOI: https://doi.org/10.2478/msp-2023-0015

KeywordsPLA, pigments, mechanical properties, DSC, colours, thermal properties

© 2023 Jacek Iwko et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Keywords
PLA, pigments, mechanical properties, DSC, colours, thermal properties