Ref. | 44.53 (3) | 25 |
Ceramic | 44.36 (2) | 16 |
Glass | 44.40 (2) | 15 |
Steel | 44.37 (2) | 19 |
Ref. | 0.799 ± 0.011 | −0.214 ± 0.015 | 0.343 ± 0.018 |
Ceramic | 0.660 ± 0.009 | −0.207 ± 0.012 | 0.165 ± 0.015 |
Glass | 0.227 ± 0.007 | −0.180 ± 0.011 | 0.259 ± 0.021 |
Steel | 0.019 ± 0.008 | −0.054 ± 0.012 | 0.462 ± 0.014 |
17-4PH as-fabricated | 0.04 | 15.85 | 4.92 | 4.79 | 0.67 | 0.71 | 0.12 | 0.27 | Bal. | |
GP1 | Wt. [%] | 0.01 | 15.8 | 4.02 | 3.9 | 0.7 | 0.7 | 0.4 | 0.29 | Bal. |
GP1 powder (EOS declaration) | <0.07 | 15–17.5 | 3–5 | 3–5 | <1 | <1 | <0.5 | 0.15–0.45 | Bal. | |
EN10088-1 | <0.07 | 15–17 | 3–5 | 3–5 | <1.5 | <0.7 | <0.6 | 5*C–0.45 | Bal. | |
ASTM A564 | <0.07 | 15–17.5 | 3–5 | 3–5 | <1 | 1 | <0.5 | 0.15–0.45 | Bal. |
Reference | – | – | – | – |
Ceramic | ∅125–250 | 1 | 0.3 | ZrO2 60%–70%, SiO2 28%–33% Al2O3 < 10% |
Glass beads | ∅100–200 | 1 | 0.3 | 70% SiO2, 10% CaO, 15% Na2O + K2O, 5% MgO |
Steel shots | ∅400–900 | 1 | 0.3 | Cr 16%–20%, Ni 7%–9%, Si 1.8%–2.2%, Mn 0.7%–1.2%, C 0.05%–0.02%, Fe-Bal. |