Synthesis of nano Mn-Zn ferrites by gel combustion method with three different fuels and investigation of their structure and properties

Published Online: 06 Oct 2020
Volume & Issue: Volume 38 (2020) - Issue 2 (June 2020)
Page range: 350 - 358
Received: 17 Oct 2018
Accepted: 23 Apr 2019
Journal Details
License
Format
Journal
eISSN
2083-134X
First Published
16 Apr 2011
Publication timeframe
4 times per year
Languages
English
Abstract

The purpose of studying the properties of zinc-manganese nanoferrite was to compare organic fuels that were produced in conditions created by the auto gel combustion method, using citric acid, glycine, and urea with different pH values: (citric acid = 6, glycine = 3 and urea = 0). The samples were prepared in stoichiometric ratios to gain Mn0.5Zn0.5Fe2O4, and all the samples were calcined in the same condition (500 °C and 30 minutes). It should be noted that the entire process of synthesis was photographed to analyze the effect of fuels during the combustion process. Combustion reactions were studied by simultaneous thermal analysis (STA), FT-IR spectroscopy, and X-ray diffraction (XRD), also the Rietveld method was used to determine the type and amount of crystalline phases. Magnetic properties of the samples were measured by vibration sample magnetometer (VSM), and their morphology and powder agglomeration was observed by field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM). Superior magnetic properties of the sample synthesized with glycine were achieved. Urea gave the smallest particle size, while citric acid produced intermediate properties.

Keywords

[1] Seyyed Ebrahimi S.A., Masoudpanah S.M., J. Magn. Magn. Mater, (2014), 77.10.1016/j.jmmm.2014.01.017Search in Google Scholar

[2] Gimenes R., Baldissera M.R., da Silva M.R.A., da Silveira C.A., Soares D.A.W., Perazolli L.A., da Silva M.R., Zaghete M.A., Ceram. Int, 1 (2012), 741.Search in Google Scholar

[3] Sutka Andris., Mezinskis Gundars., Front. Mater. Sci, 2 (2012), 128.10.1007/s11706-012-0167-3Search in Google Scholar

[4] Ghobeiti Hasab M., Ebrahimi S.A., Badiei A., J. Non.-Cryst. Solids, 8-10 (2007), 814.10.1016/j.jnoncrysol.2006.12.048Search in Google Scholar

[5] Murugesan C., Mdgazzali P.M., Chandrasekaran G., J. Mater. Sci.-Mater. El, 8 (2013), 3136.10.1007/s10854-013-1222-2Search in Google Scholar

[6] Hajarpour S., Gheisari KH., Honarbakhsh Raouf A., J. Magn. Magn. Mater, 329 (2013), 165.10.1016/j.jmmm.2012.10.023Search in Google Scholar

[7] Tonoilo J.C., Lima M.D., Takimi A.S., Bergmann C.P., Mater. Res. Bull, 3 (2005), 561.10.1016/j.materresbull.2004.07.019Search in Google Scholar

[8] Vasanthi V., Shanmugavani A., Sanjeeviraja C., Kalai Selvan R., J. Magn. Magn. Mater, 13 (2012), 2100.10.1016/j.jmmm.2012.02.018Search in Google Scholar

[9] Hwang C.C., Tsai J.S., Huang T.H., Mater. Chem. Phys, 2-3 (2005), 330.10.1016/j.matchemphys.2005.03.056Search in Google Scholar

[10] Pedzich Z., Bucko M.M., Krolikowski M., Bakalarska M., Babiarz J., J. Eur. Ceram. Soc, 6 (2004), 1053.10.1016/S0955-2219(03)00386-8Search in Google Scholar

[11] Hou J.G., Qu Y.F., Ma W.B., Sun Q.C., J. Sol.-Gel. Sci. Techn, 1 (2007), 15.10.1007/s10971-007-1600-4Search in Google Scholar

[12] Bakhshi H., Shokuhfar A., Seyyed Afghahi S.S., Ceram. Int, 9 (2015), 10736.10.1016/j.ceramint.2015.05.009Search in Google Scholar

[13] Motevalian A., Salem S., Particuology, (2016), 108.10.1016/j.partic.2015.03.005Search in Google Scholar

[14] Mohamed R.M., Rashad M.M., Haraz F., Sigmund W., J. Magn. Magn. Mater, 14 (2010), 2058.10.1016/j.jmmm.2010.01.034Search in Google Scholar

[15] Rasly M., Rashad M.M., J. Magn. Magn. Mater, (2013), 58.10.1016/j.jmmm.2013.02.038Search in Google Scholar

[16] Rashad M.M., Turky A.O., Kandil A.T., J. Mater. Sci.-Mater. El, 9 (2013) 3284.10.1007/s10854-013-1244-9Search in Google Scholar

[17] Rashad M.M., J. Mater. Sci.-Mater. El, 4 (2012), 882.10.1007/s10854-011-0513-8Search in Google Scholar

[18] Bahadur D., Rajakumar S., Kumar A., J. Chem. Sci, 1 (2006), 15.10.1007/BF02708761Search in Google Scholar

[19] Abu el Fadl A., Hassan A.M., Mahmoud M.H., Tatarchuk T., Yaremiy I.P., Gismelssed A.M., Ahmed M.A., J. Magn. Magn. Mater, (2019), 192.Search in Google Scholar

[20] Ahmed M.A., Hassan H.E., Eltabey M.M., Latla K., Tatarchuk T.R., Physica. B, (2018), 195.Search in Google Scholar

[21] Rajesh Babu B., Tatarchuk T., Mater. Chem. Phys, (2018) 534.10.1016/j.matchemphys.2017.12.084Search in Google Scholar

[22] Kane S.N., Raghuvanshi S., Satalkar M., Reddy V.R., Deshpande U.P., Tatarchuk T.R., Mazaleyrat F., AIP. Conf. Proc, 1 (2018), 030089.Search in Google Scholar

[23] Tatarchuk Tetiana., Bououdina M., Judith Vijaya J., John Kennedy L., Nanophysics, Nanomaterials, Interface Studies, and Applications, Springer, Lviv, 2016.Search in Google Scholar

[24] Hu P., Yang H.B., Pan D.A., Wang H., Tian J.J., Zhang S.G., Wang X.F., A.Volinsky A., J. Magn. Magn. Mater, 1 (2010) 173.Search in Google Scholar

[25] Bakhshi H., Shokuhfar A., Vahdati N., Int. j. Min. Met. Mater, 9 (2016), 1104.10.1007/s12613-016-1328-7Search in Google Scholar

[26] Waqas H., Qureshi A.H., J. Therm. Anal. Calorim, 2 (2009), 355.10.1007/s10973-009-0289-8Search in Google Scholar

[27] Costa A.C.F.M, Morelli M.R., Kiminami R.H., J. Mater. Synth. Process, 6 (2001), 347.10.1023/A:1016356623401Search in Google Scholar

[28] Costa A.C.F.M., Silva V.J., Xin C.C., Viera D.A., Cornejo D.R., Kiminami R.H.G.A., J. Alloy. Compd, 2 (2010), 503.10.1016/j.jallcom.2009.10.065Search in Google Scholar

[29] Tatarchuk T.R., Bououdina M., Paliychuk N.D., Yaremiy I.P., Moklyak V.V., J. Alloy. Compd, (2017), 777.10.1016/j.jallcom.2016.10.067Search in Google Scholar

[30] Tatarchuk T.R., Paliychuk N.D., Bououdina M., Al Najar B., Pacia M., Macyk W., Shyichunk A., J. Alloy. Compd, (2018), 1256.10.1016/j.jallcom.2017.10.103Search in Google Scholar

[31] Szczygiel I., Winiarska K., Bien Ko A., Suracka K., Gaworska Koniarek D., J. Alloy. Compd, (2014), 1.10.1016/j.jallcom.2014.03.109Search in Google Scholar

[32] Maensiri S., Chivalrat M., Boonchom B., Seraphin Supapan., Scripta. Mater, 9 (2007), 797.10.1016/j.scriptamat.2006.09.033Search in Google Scholar

[33] Gabal M.A., Abdel Daiem A.M., Al Angari Y.M., Ismail I.M., Polyhedron, (2013), 105.10.1016/j.poly.2013.04.027Search in Google Scholar

[34] Wang W., Zang C., Jiao Q., J. Magn. Magn. Mater, (2014), 116.10.1016/j.jmmm.2013.08.057Search in Google Scholar

Recommended articles from Trend MD

Plan your remote conference with Sciendo