<abstract xmlns="http://www.w3.org/1999/xhtml">

<sec>
<h3>Background</h3>
<p>Selection of the appropriate curing time and light direction may enable the appropriate shear bond strength to be obtained and avoid enamel fracture during debonding.</p>
</sec>
<sec>
<h3>Aims</h3>
<p>To determine the effects of different curing times and light directions on the shear bond strengths of ceramic and stainless steel brackets.</p>
</sec>
<sec>
<h3>Method</h3>
<p>Ninety-two recently extracted, upper premolars were randomly assigned to six groups. Either stainless steel or ceramic brackets were bonded to the buccal surfaces of the teeth. Group 1, stainless steel brackets cured for 40 seconds from buccal surface; Group II, stainless steel brackets cured for 40 seconds from palatal surface; Group III, stainless steel brackets cured for 80 seconds from palatal surface; Group IV, ceramic brackets cured for 40 seconds from the buccal surface; Group V, ceramic brackets cured for 40 seconds from the palatal surface; Group VI, ceramic brackets cured for 80 seconds from the palatal surface. The shear bond strength was measured with a universal testing machine and the resin remaining after debonding scored with the Adhesive Remnant Index (ARI). The data were analysed with the one-way ANOVA, Tukey’s HSD test and the Kruskal-Wallis test. Associations between the ARI and shear bond strength were determined with Pearson’s correlation coefficient.</p>
</sec>
<sec>
<h3>Results</h3>
<p>Group IV (ceramic brackets cured for 40 seconds from buccal surface) had the highest shear bond strength (21.26 MPa) and Group II (metal brackets cured for 40 seconds from palatal surface) had the lowest shear bond strength (6.95 MPa).There was no significant difference in ARI scores among the groups. The association between the ARI scores and bond strength values was not statistically significant.</p>
</sec>
<sec>
<h3>Conclusions</h3>
<p>Curing from the buccal surface for 40 seconds gave unacceptably high shear bond strength values for both stainless steel and ceramic brackets. Lower shear bond strengths occurred when the light was directed from the palatal surface, but a shorter curing time is more likely to be preferred by clinicians. Future studies should investigate the possibility of reducing the curing time for both brackets.</p>
</sec>
</abstract>

Background
Selection of the appropriate curing time and light direction may enable the appropriate shear bond strength to be obtained and avoid enamel fracture during debonding.


Aims
To determine the effects of different curing times and light directions on the shear bond strengths of ceramic and stainless steel brackets.


Method
Ninety-two recently extracted, upper premolars were randomly assigned to six groups. Either stainless steel or ceramic brackets were bonded to the buccal surfaces of the teeth. Group 1, stainless steel brackets cured for 40 seconds from buccal surface; Group II, stainless steel brackets cured for 40 seconds from palatal surface; Group III, stainless steel brackets cured for 80 seconds from palatal surface; Group IV, ceramic brackets cured for 40 seconds from the buccal surface; Group V, ceramic brackets cured for 40 seconds from the palatal surface; Group VI, ceramic brackets cured for 80 seconds from the palatal surface. The shear bond strength was measured with a universal testing machine and the resin remaining after debonding scored with the Adhesive Remnant Index (ARI). The data were analysed with the one-way ANOVA, Tukey’s HSD test and the Kruskal-Wallis test. Associations between the ARI and shear bond strength were determined with Pearson’s correlation coefficient.


Results
Group IV (ceramic brackets cured for 40 seconds from buccal surface) had the highest shear bond strength (21.26 MPa) and Group II (metal brackets cured for 40 seconds from palatal surface) had the lowest shear bond strength (6.95 MPa).There was no significant difference in ARI scores among the groups. The association between the ARI scores and bond strength values was not statistically significant.


Conclusions
Curing from the buccal surface for 40 seconds gave unacceptably high shear bond strength values for both stainless steel and ceramic brackets. Lower shear bond strengths occurred when the light was directed from the palatal surface, but a shorter curing time is more likely to be preferred by clinicians. Future studies should investigate the possibility of reducing the curing time for both brackets.

Changes in shear bond strength of ceramic and stainless steel brackets with different visible light curing times and directions

Australasian Orthodontic Journal

This work is licensed under the Creative Commons Attribution 4.0 International License.

Background
Selection of the appropriate curing time and light direction may enable the appropriate shear bond strength to be obtained and avoid enamel fracture...

Changes in shear bond strength of ceramic and stainless steel brackets with different visible light curing times and directions

Published Online: Dec 14, 2023

Page range: 153 - 157

Received: Oct 01, 2008

Accepted: Oct 01, 2009

DOI: https://doi.org/10.2478/aoj-2009-0023

© 2009 Farzin Heravi et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.