<abstract xmlns="http://www.w3.org/1999/xhtml"> A series of glasses of the composition 20Na2-O-15CaO-5B2O3-5SiO2-(55 - x) P2O5:xMnO2, was prepared and characterized by XRD, DSC, SEM, and Raman techniques. The samples were later immersed in simulated body fluid (SBF) for checking the potential growth of hydroxyapatite layer (HA). Experiments confirmed that addition of manganese oxide leads to structural changes of the glasses. With increasing content of MnO2, the surface of the samples became more congenial for improving the growth of HA. The formation of HA layer on the surface of the samples was confirmed just after seven days of immersion. The growth rate of HA has gradually increased with the increase of MnO2 content.</abstract>

A series of glasses of the composition 20Na2-O-15CaO-5B2O3-5SiO2-(55 - x) P2O5:xMnO2, was prepared and characterized by XRD, DSC, SEM, and Raman techniques. The samples were later immersed in simulated body fluid (SBF) for checking the potential growth of hydroxyapatite layer (HA). Experiments confirmed that addition of manganese oxide leads to structural changes of the glasses. With increasing content of MnO2, the surface of the samples became more congenial for improving the growth of HA. The formation of HA layer on the surface of the samples was confirmed just after seven days of immersion. The growth rate of HA has gradually increased with the increase of MnO2 content.

Are the phosphorus-rich Na2O–CaO–B2O3–SiO2–P2O5 glasses bioactive and what is an influence of doping with manganese oxide?

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Are the phosphorus-rich NaO–CaO–BO–SiO–PO glasses bioactive and what is an influence of doping with manganese oxide?

A series of glasses of the composition 20Na2-O-15CaO-5B2O3-5SiO2-(55 - x) P2O5:xMnO2, was prepared and characterized by XRD, DSC, SEM, and Raman techniques....

Are the phosphorus-rich Na₂O–CaO–B₂O₃–SiO₂–P₂O₅ glasses bioactive and what is an influence of doping with manganese oxide?

Published Online: Mar 20, 2018

Page range: 760 - 766

Received: Dec 23, 2016

Accepted: Oct 17, 2017

DOI: https://doi.org/10.1515/msp-2017-0093

Keywords
bioactive glass, Simulated Body Fluid, Mn ions as dopant, hydroxyapatite grains shape

© 2018

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Are the phosphorus-rich Na2O–CaO–B2O3–SiO2–P2O5 glasses bioactive and what is an influence of doping with manganese oxide?

Published Online: Mar 20, 2018

Page range: 760 - 766

Received: Dec 23, 2016

Accepted: Oct 17, 2017

DOI: https://doi.org/10.1515/msp-2017-0093

Keywordsbioactive glass, Simulated Body Fluid, Mn ions as dopant, hydroxyapatite grains shape

© 2018

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Are the phosphorus-rich Na₂O–CaO–B₂O₃–SiO₂–P₂O₅ glasses bioactive and what is an influence of doping with manganese oxide?

Keywords
bioactive glass, Simulated Body Fluid, Mn ions as dopant, hydroxyapatite grains shape