<abstract xmlns="http://www.w3.org/1999/xhtml"> LaCrO3 perovskite nanopowders were successfully prepared via a sol-gel method using stoichiometric proportion of materials containing lanthanum and chromium in stearic acid complexing agent. Structural analysis of LaCrO3 indicated an octahedral framework in its XRD pattern bearing crystallite size in the range of 28 nm. The particle sizes were confirmed by morphological scanning of the sample. The optical properties of LaCrO3 nanopowders clearly indicated an interesting optical activity of LaCrO3 in the UV and visible ranges. The degradation activation energy (Ed) was calculated from the output of a moderate thermal programming profile at about 207.97 kJ·mol-1 using Kissinger equation. Capacity, impedance and AC resistance of the perovskites was obtained at 2.970 nF, 2.522 MΩ and 16.19 MΩ, respectively. </abstract>

LaCrO3 perovskite nanopowders were successfully prepared via a sol-gel method using stoichiometric proportion of materials containing lanthanum and chromium in stearic acid complexing agent. Structural analysis of LaCrO3 indicated an octahedral framework in its XRD pattern bearing crystallite size in the range of 28 nm. The particle sizes were confirmed by morphological scanning of the sample. The optical properties of LaCrO3 nanopowders clearly indicated an interesting optical activity of LaCrO3 in the UV and visible ranges. The degradation activation energy (Ed) was calculated from the output of a moderate thermal programming profile at about 207.97 kJ·mol-1 using Kissinger equation. Capacity, impedance and AC resistance of the perovskites was obtained at 2.970 nF, 2.522 MΩ and 16.19 MΩ, respectively.

Kinetic properties and structural analysis of LaCrO3 nanoparticles

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Kinetic properties and structural analysis of LaCrO nanoparticles

LaCrO3 perovskite nanopowders were successfully prepared via a sol-gel method using stoichiometric proportion of materials containing lanthanum and chromium in...

Kinetic properties and structural analysis of LaCrO₃ nanoparticles

Published Online: Jul 26, 2017

Page range: 368 - 373

Received: Jan 10, 2016

Accepted: Feb 19, 2017

DOI: https://doi.org/10.1515/msp-2017-0043

Keywords
LaCrO3, nanoperovskite, sol-gel, kinetic parameter

© 2017

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Kinetic properties and structural analysis of LaCrO3 nanoparticles

Published Online: Jul 26, 2017

Page range: 368 - 373

Received: Jan 10, 2016

Accepted: Feb 19, 2017

DOI: https://doi.org/10.1515/msp-2017-0043

KeywordsLaCrO3, nanoperovskite, sol-gel, kinetic parameter

© 2017

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Kinetic properties and structural analysis of LaCrO₃ nanoparticles

Keywords
LaCrO3, nanoperovskite, sol-gel, kinetic parameter