Influence of different synthesis conditions on properties of oleic acid-coated-Fe3O4 nanoparticles

Published Online: 13 Mar 2015
Volume & Issue: Volume 33 (2015) - Issue 1 (March 2015)
Page range: 100 - 106
Received: 15 Jun 2014
Accepted: 03 Dec 2014
Journal Details
License
Format
Journal
eISSN
2083-134X
First Published
16 Apr 2011
Publication timeframe
4 times per year
Languages
English
Abstract

In the present paper, iron oxide nanoparticles coated by oleic acid have been synthesized in different conditions by coprecipitation method. For investigating the effect of time spent on adding the oleic acid to the precursor solution, two different processes have been considered. The as synthesized samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and Fourier transform infrared spectroscopy (FT-IR). Magnetic measurement was carried out at room temperature using a vibrating sample magnetometer (VSM). The results show that the magnetic nanoparticles decorated with oleic acid decreased the saturation of magnetization. From the data, it can also be concluded that the magnetization of Fe3O4/oleic acid nanoparticles depends on synthesis conditions.

Keywords

[1] REISS G., HUTTEN A., Nat. Mater., 4 (2005), 725.10.1038/nmat1494Search in Google Scholar

[2] TAN H., XUE J.M., SHUTER B., LI X., WANG J., Adv. Funct. Mater, 20 (2010), 722.10.1002/adfm.200901820Search in Google Scholar

[3] KIM J., LEE J.E., LEE S.H., YU J.H., LEE J.H., PARK T.G., HYEON T., Adv. Mater, 20 (2008), 478.10.1002/adma.200701726Search in Google Scholar

[4] WANG C., DAIMON H., SUN S., Nano Lett., 9 (2009), 1493.10.1021/nl8034724Search in Google Scholar

[5] SUN S., ZENG H., ROBINSON D.B., RAOUX S., RICE P.M., WANG S.X., LI G., J. Am. Chem. Soc., 126 (2004), 273.10.1021/ja0380852Search in Google Scholar

[6] ZHANG Y., KOHLER N., ZHANG M., Biomaterials, 23 (2002), 1553.10.1016/S0142-9612(01)00267-8Search in Google Scholar

[7] O’HANDLEY R.C., Modern Magnetic Materials: Principles and Applications, John Wiley & Sons, New York, 2000.Search in Google Scholar

[8] LESLIE-PELECKY D.L., RIEKE R.D., Chem. Mater., 8 (1996), 1770.10.1021/cm960077fSearch in Google Scholar

[9] LAURENT S., FORGE D., PORT M., ROCH A., ROBIC C., ELS V.L., MULLER R., Chem. Rev., 108 (2008), 2064.10.1021/cr068445eSearch in Google Scholar

[10] CORNELL R.M., SCHERTMANN U., The Iron Oxides: Structure, Properties, Reactions, Occurrence and Uses, VCH Publishers, Weinheim, Germany, 2003.10.1002/3527602097Search in Google Scholar

[11] HARRIS L.A., Polymer stabilized magnetite nanoparticles, Ph.D. Thesis, Virginia Polytechnic Institute and State University, Virginia, 2002.Search in Google Scholar

[12] PARDOE H., CHUA-ANUSORN W., ST PIERRE T.G., DOBSON J., J. Magn. Magn. Mater., 225 (2001), 41.10.1016/S0304-8853(00)01226-9Search in Google Scholar

[13] GHOTBI M.Y., HUSSEIN M.B., J. Phys. Chem. Solids, 73 (2012), 936.10.1016/j.jpcs.2012.02.031Search in Google Scholar

[14] CHOI S.H., ZHANG Y.P., GOPALAN A., LEE K.P., KANG H.D., Colloid. Surface. A, 256 (2005), 165.10.1016/j.colsurfa.2004.07.022Search in Google Scholar

[15] JIAN P., FEN Z., LU L., LIANG T., LI Y., WEI CH., HUI L., JING-BO T., LI-XIANG W., T. Nonferr. Metal. Soc., 18 (2008), 393.Search in Google Scholar

[16] KAYAL S., RAMANUJAN R.V., Mat. Sci. Eng. C-Mater., 30 (2010), 484.10.1016/j.msec.2010.01.006Search in Google Scholar

[17] TOMIKATA A., KOSHI T., HATSUGAI SH., YAMADA T., TAKEMURA Y., J. Magn. Magn. Mater., 323 (2011), 1398.10.1016/j.jmmm.2010.11.054Search in Google Scholar

[18] LI D., JIANG D., CHEN M., XIE J., WU Y., DANG SH., ZHANG J., Mater. Lett., 64 (2010), 2462.10.1016/j.matlet.2010.08.025Search in Google Scholar

[19] GNANAPRAKASH G., MAHADEVAN S., JAYAKUMAR T., KALYANASUNDARAM P., PHILIPH J., RAJ B., Mater. Chem. Phys., 103 (2007), 168.10.1016/j.matchemphys.2007.02.011Search in Google Scholar

[20] WANG CH. Y., HONG J. M., CHEN G., ZHANG Y., GU N., Chinese Chem. Lett., 21 (2010), 179.10.1016/j.cclet.2009.10.024Search in Google Scholar

[21] LIN J., WANG CH., LEE M., J. Magn. Magn. Mater., 332 (2013), 192.10.1016/j.jmmm.2012.12.037Search in Google Scholar

[22] FENG J., MAO J., WEN X., TU M., J. Alloy. Compd., 509 (2011), 9093.10.1016/j.jallcom.2011.06.053Search in Google Scholar

[23] MAITY D., AGRAWAL D.C., J. Magn. Magn. Mater., 308 (2007), 46.10.1016/j.jmmm.2006.05.001Search in Google Scholar

[24] WEI Y., HAN B., HU X., LIN Y., WANG X., DENG X., Procedia Eng., 27 (2012), 632.10.1016/j.proeng.2011.12.498Search in Google Scholar

[25] INGRAM D., KOTSMAR C., YOON K.Y., SHAO S., HUH CH., BRYANT S., MILNER TH., JOHNSTON K., J. Colloid Interf. Sci., 351(2010), 225.10.1016/j.jcis.2010.06.04820719327Search in Google Scholar

[26] VERIANSYAH B., KIM J.D., MIN B.K., KIM J., Mater. Lett., 64 (2010), 2197.10.1016/j.matlet.2010.07.018Search in Google Scholar

[27] AHMAD M.A., OKASHA N., EL-DEK S.I., Ceram. Int., 36 (2010), 1529.10.1016/j.ceramint.2010.02.017Search in Google Scholar

[28] CABRERA L., GUTIERREZ S., MENENDEZ N., MORALES M.P., HERRASTI P., Electrochim. Acta, 53 (2008), 3436.10.1016/j.electacta.2007.12.006Search in Google Scholar

[29] ALIAHMAD M., NASIRI MOGHADDAM N., Mater. Sci.-Poland, 31 (2013), 264.10.2478/s13536-012-0100-6Search in Google Scholar

[30] CULLITY B.D., Introduction to Magnetic Materials, Addison-Wesley Publishing Company, Reading, Massachusetts, 1972.Search in Google Scholar

[31] FAIYAS A.P.A., VINOD E.M., JOSEPH J., GANESAN R., PANDEY R.K., J. Magn. Magn. Mater., 322 (2010), 400.10.1016/j.jmmm.2009.09.064Search in Google Scholar

[32] KHORSAND ZAK A., ABD MAJID W.H., ABRISHAMI M.E., YOUSEFI R., Solid State Sci., 13 (2011), 251.10.1016/j.solidstatesciences.2010.11.024Search in Google Scholar

[33] LEE S.Y., HARRIS M.T., J. Coll. Interf. Sci., 293 (2006), 401.10.1016/j.jcis.2005.06.06216054635Search in Google Scholar

[34] GIRI J., THAKURTA S.G., BELLARE J., NIGAM A.K., BAHADUR D., J. Magn. Magn. Mater., 293 (2005), 62.10.1016/j.jmmm.2005.01.044Search in Google Scholar

[35] AHN Y., CHOI E.J., KIM E.H., Rev. Adv Mater. Sci, 5 (2003), 477.Search in Google Scholar

[36] NAKAMOTO K., Infrared and Raman Spectra of Inorganic and Coordination Compounds, Wiley, New York, 2009.10.1002/9780470405888Search in Google Scholar

[37] REN Y., LIMURA K., KATO T., Langmuir, 17 (2001), 2688.10.1021/la000872eSearch in Google Scholar

[38] WILLIS A.L., TURRO N.J., O’BRIEN S., Chem. Mater., 17 (2005), 5970.10.1021/cm051370vSearch in Google Scholar

[39] MONTAGNE F., MONDAIN-MONVAL O., PICHOT C., MOZZANEGA H., ELAISSARI A., J. Magn. Magn. Mater., 250 (2002), 302.10.1016/S0304-8853(02)00412-2Search in Google Scholar

[40] MORALES M.P., ANDRES-VERGES M., VEINTEMILLAS-VERDAGUER S., MONTERO M.I., SERNA C.J., J. Magn. Magn. Mater., 203 (1999), 146.10.1016/S0304-8853(99)00278-4Search in Google Scholar

[41] SKOMSKI R., Simple Models of Magnetism, Oxford University, New York, 2008.10.1093/acprof:oso/9780198570752.001.0001Search in Google Scholar

[42] RAJENDRAN M., PULLAR R.C., BHATTACHARYA A.K., DAS D., CHINTALAPUDI S.N., MAJUMDAR C.K., J. Magn. Magn. Mater., 232 (2001), 71. 10.1016/S0304-8853(01)00151-2Search in Google Scholar

Recommended articles from Trend MD

Plan your remote conference with Sciendo