XPS Analysis of AISI 304L Stainless Steel Surface after Electropolishing
, , and
Apr 10, 2015
About this article
Published Online: Apr 10, 2015
Page range: 21 - 29
DOI: https://doi.org/10.1515/adms-2015-0004
Keywords
© by K. Rokosz
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.
In the paper, the passive surface layers of AISI 304L after standard (EP50) and very-high-current density electropolishing (EP1000) in a mixture of orthophosphoric and sulfuric acids in a 1:4 ratio, are presented. The main finding of the presented studies is enrichment of the steel surface film in chromium: total chromium to total iron ratio was equal to 6.6 after EP50 and to 2.8 after EP1000; on the other hand, chromium compounds to iron compounds ratio was equal to 10.1 after EP50, and 3.9 after EP1000.