<abstract xmlns="http://www.w3.org/1999/xhtml">This paper presents an investigation in which bio-based polyamide 10.10 was used as a polymer matrix. Composites were reinforced in three different ways including: 10 wt% and 30 wt% of walnut shell flour as well as 30 wt% of glass fibres. The composites were prepared by injection moulding. mechanical properties (tensile strength (σ<italic>t</italic>), modulus of elasticity (<italic>E</italic><italic>t</italic>) as well as flexural modulus (<italic>E</italic><italic>f</italic>) and flexural stress at 3.5% strain (σ<italic>f</italic>)) were obtained. The mechanical data of analysis showed that tensile strength and tensile stiffness significantly decreased after four years of storage. another state was noted for the bending module, where the decrease in value was at a level of 5% compared to results obtained immediately after injection. additionally, sem images were taken to assess the distribution of particles and the adhesion of fillers to the matrix.</abstract>

This paper presents an investigation in which bio-based polyamide 10.10 was used as a polymer matrix. Composites were reinforced in three different ways including: 10 wt% and 30 wt% of walnut shell flour as well as 30 wt% of glass fibres. The composites were prepared by injection moulding. mechanical properties (tensile strength (σt), modulus of elasticity (Et) as well as flexural modulus (Ef) and flexural stress at 3.5% strain (σf)) were obtained. The mechanical data of analysis showed that tensile strength and tensile stiffness significantly decreased after four years of storage. another state was noted for the bending module, where the decrease in value was at a level of 5% compared to results obtained immediately after injection. additionally, sem images were taken to assess the distribution of particles and the adhesion of fillers to the matrix.

The effect of long-term storage on the mechanical properties of composites based on polyamide 10.10 derived from renewable sources

Institute of Material Engineering, Faculty of Mechanical Engineering

Technical Transactions

This work is licensed under the Creative Commons Attribution-ShareAlike 4.0 Public License.

This paper presents an investigation in which bio-based polyamide 10.10 was used as a polymer matrix. Composites were reinforced in three different ways...

The effect of long-term storage on the mechanical properties of composites based on polyamide 10.10 derived from renewable sources

Pubblicato online: 21 mag 2020

Pagine: 167 - 175

Ricevuto: 20 lug 2018

DOI: https://doi.org/10.4467/2353737XCT.18.123.8898

Parole chiave
bio-based composite, mechanical properties, injection moulding, Hiprolon 211

© 2019 Stanisław Kuciel et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-ShareAlike 4.0 Public License.

The effect of long-term storage on the mechanical properties of composites based on polyamide 10.10 derived from renewable sources

Pubblicato online: 21 mag 2020

Pagine: 167 - 175

Ricevuto: 20 lug 2018

DOI: https://doi.org/10.4467/2353737XCT.18.123.8898

Parole chiavebio-based composite, mechanical properties, injection moulding, Hiprolon 211

© 2019 Stanisław Kuciel et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-ShareAlike 4.0 Public License.

Parole chiave
bio-based composite, mechanical properties, injection moulding, Hiprolon 211