<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml">We have studied La0.67Sr0.33MnO3 (LSMO) thin films with temperature of metal-insulator (<italic>T</italic>MI) transition enhanced to above 400 K, and we estimated characteristic electrical transport mechanisms for these films. We have fitted the measured resistivity vs. temperature ρ(<italic>T</italic>) dependence in a wide temperature range 4-500 K using different mechanisms of the electrical transport in different parts of ρ(<italic>T</italic>). In addition to the narrow temperature range around <italic>T</italic>MI very well agreement was found. We found out that the Debye's temperature was also increased (Θ<italic>D</italic> ≈ 840 K) probably due to the change in crystallization of LSMO films.</abstract>

We have studied La0.67Sr0.33MnO3 (LSMO) thin films with temperature of metal-insulator (TMI) transition enhanced to above 400 K, and we estimated characteristic electrical transport mechanisms for these films. We have fitted the measured resistivity vs. temperature ρ(T) dependence in a wide temperature range 4-500 K using different mechanisms of the electrical transport in different parts of ρ(T). In addition to the narrow temperature range around TMI very well agreement was found. We found out that the Debye's temperature was also increased (ΘD ≈ 840 K) probably due to the change in crystallization of LSMO films.

Characterization of Electrical Transport in Lsmo with Enhanced Temperature of Metal-Insulator Transition

Institute of Electrical Engineering, SAS, Dúbravská cesta 9, 841 04 Bratislava, Slovakia

Journal of Electrical Engineering

We have studied La0.67Sr0.33MnO3 (LSMO) thin films with temperature of metal-insulator (TMI) transition enhanced to above 400 K, and we estimated...

Characterization of Electrical Transport in Lsmo with Enhanced Temperature of Metal-Insulator Transition

Pubblicato online: 17 set 2012

Pagine: 270 - 272

DOI: https://doi.org/10.2478/v10187-012-0039-1

Parole chiave
LSMO thin film, electrical transport, Debye temperature

This content is open access.

Characterization of Electrical Transport in Lsmo with Enhanced Temperature of Metal-Insulator Transition

Pubblicato online: 17 set 2012

Pagine: 270 - 272

DOI: https://doi.org/10.2478/v10187-012-0039-1

Parole chiaveLSMO thin film, electrical transport, Debye temperature

This content is open access.

Parole chiave
LSMO thin film, electrical transport, Debye temperature