<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>LiMn2O4 is an attractive candidate cathode material for Li-ion rechargeable batteries, but it suffers from severe capacity fading, especially at higher temperature (55 °C) during charging/discharging processes. Recently, many attempts have been made to synthesize modified LiMn2O4. In this work, a new study on the synthesis of pure and U4+-doped nano lithium manganese oxide [LiMn2−x
                        UxO4, (x = 0:00, 0.01, 0.03)] via solid-state method was introduced. The synthesized LiMn1:97U0:03O4 was irradiated by γ-radiation (10 and 30 kGy). The green samples and the resulting spinel products were characterized using thermogravimetric and differential thermal analysis (TG/DTA), X-ray diffraction (XRD), infrared (IR), and scanning electron microscopy (SEM) measurements. XRD and SEM studies revealed nano-sized particles in all prepared samples. Direct-current (DC) electrical conductivity measurements indicated that these samples are semiconductors and the activation energies decrease with increasing rare-earth U4+ content and γ-irradiation. ΔEa equals to 0.304 eV for LiMn1:99U0:01O4, ΔEa is 0.282 eV for LiMn1:97U0:03O4 and decreases to ΔEa = 0:262 eV for γ-irradiated LiMn1:97U0:03O4 nano spinel. The data obtained for the investigated samples increase their attractiveness in modern electronic technology.</p></abstract>

LiMn2O4 is an attractive candidate cathode material for Li-ion rechargeable batteries, but it suffers from severe capacity fading, especially at higher temperature (55 °C) during charging/discharging processes. Recently, many attempts have been made to synthesize modified LiMn2O4. In this work, a new study on the synthesis of pure and U4+-doped nano lithium manganese oxide [LiMn2−x
                        UxO4, (x = 0:00, 0.01, 0.03)] via solid-state method was introduced. The synthesized LiMn1:97U0:03O4 was irradiated by γ-radiation (10 and 30 kGy). The green samples and the resulting spinel products were characterized using thermogravimetric and differential thermal analysis (TG/DTA), X-ray diffraction (XRD), infrared (IR), and scanning electron microscopy (SEM) measurements. XRD and SEM studies revealed nano-sized particles in all prepared samples. Direct-current (DC) electrical conductivity measurements indicated that these samples are semiconductors and the activation energies decrease with increasing rare-earth U4+ content and γ-irradiation. ΔEa equals to 0.304 eV for LiMn1:99U0:01O4, ΔEa is 0.282 eV for LiMn1:97U0:03O4 and decreases to ΔEa = 0:262 eV for γ-irradiated LiMn1:97U0:03O4 nano spinel. The data obtained for the investigated samples increase their attractiveness in modern electronic technology.

Synthesis, effect of γ-ray and electrical conductivity of uranium doped nano LiMn2O4 spinels for applications as positive electrodes in Li-ion rechargeable batteries

Chemistry Department, Faculty of Science, Tanta University, Tanta, Egypt

Chemistry Department, College of Applied Sciences, Umm Al-Qura University, Makkah, Saudi Arabia

Chemistry Department, Faculty of Science, Jazan University, Jazan, Saudi Arabia

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

LiMn2O4 is an attractive candidate cathode material for Li-ion rechargeable batteries, but it suffers from severe capacity fading, especially at higher...

Synthesis, effect of γ-ray and electrical conductivity of uranium doped nano LiMn2O4 spinels for applications as positive electrodes in Li-ion rechargeable batteries

Pubblicato online: 19 dic 2014

Pagine: 571 - 577

DOI: https://doi.org/10.2478/s13536-014-0236-7

Parole chiave
U4+-doped nano lithium manganates, γ-ray effect, electrical conductivity

© 2014 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Synthesis, effect of γ-ray and electrical conductivity of uranium doped nano LiMn2O4 spinels for applications as positive electrodes in Li-ion rechargeable batteries

Pubblicato online: 19 dic 2014

Pagine: 571 - 577

DOI: https://doi.org/10.2478/s13536-014-0236-7

Parole chiaveU4+-doped nano lithium manganates, γ-ray effect, electrical conductivity

© 2014 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
U4+-doped nano lithium manganates, γ-ray effect, electrical conductivity