<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>(Na0.52K0.44Li0.04)0.97La0.01Ta0.20Nb0.80O3 (KNLTN-La0.01) lead-free subtransparent ceramics was prepared by a conventional sintering technique. The structure and the optical properties of the ceramics were investigated. The room temperature crystallographic indexing revealed the ABO3 perovskite type, tetragonal phase and P4mm point group in the ceramics. The surface and fractured surface SEM micrographs showed a dense microstructure with few micropores in KNLTN-La0.01 ceramics, which was obviously better than for the pure KNLTN ceramics. The refractive indexes of the films were investigated by an ellipsometer and the results show that the KNLTN-La0.01 subtransparent ceramics reveals significant wavelength dependent dispersion. The refractive index ranges from 2.14 to 2.06 with the wavelength increase from 380 nm to 900 nm. The dispersive behavior was analyzed by three parameters of Cauchy dispersion model and the values of the parameters A, B and C are 2.0610±0.0005, 0.0054±0.0003 and 0.00069±0.00004, respectively.</p></abstract>

(Na0.52K0.44Li0.04)0.97La0.01Ta0.20Nb0.80O3 (KNLTN-La0.01) lead-free subtransparent ceramics was prepared by a conventional sintering technique. The structure and the optical properties of the ceramics were investigated. The room temperature crystallographic indexing revealed the ABO3 perovskite type, tetragonal phase and P4mm point group in the ceramics. The surface and fractured surface SEM micrographs showed a dense microstructure with few micropores in KNLTN-La0.01 ceramics, which was obviously better than for the pure KNLTN ceramics. The refractive indexes of the films were investigated by an ellipsometer and the results show that the KNLTN-La0.01 subtransparent ceramics reveals significant wavelength dependent dispersion. The refractive index ranges from 2.14 to 2.06 with the wavelength increase from 380 nm to 900 nm. The dispersive behavior was analyzed by three parameters of Cauchy dispersion model and the values of the parameters A, B and C are 2.0610±0.0005, 0.0054±0.0003 and 0.00069±0.00004, respectively.

The structure and optical properties of lead-free transparent KNLTN-La0.01 ceramics prepared by conventional sintering technique

Department of Applied Science, Harbin University of Science and Technology, Harbin, 150080, PR China

Department of Physics, Harbin Institute of Technology, Harbin, 150001, PR China

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

(Na0.52K0.44Li0.04)0.97La0.01Ta0.20Nb0.80O3 (KNLTN-La0.01) lead-free subtransparent ceramics was prepared by a conventional sintering technique. The structure...

The structure and optical properties of lead-free transparent KNLTN-La0.01 ceramics prepared by conventional sintering technique

Pubblicato online: 19 dic 2014

Pagine: 597 - 603

DOI: https://doi.org/10.2478/s13536-014-0226-9

Parole chiave
lead-free ceramics, subtransparent ceramics, optical properties, refractive index dispersion, Cauchy model

© 2014 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The structure and optical properties of lead-free transparent KNLTN-La0.01 ceramics prepared by conventional sintering technique

Pubblicato online: 19 dic 2014

Pagine: 597 - 603

DOI: https://doi.org/10.2478/s13536-014-0226-9

Parole chiavelead-free ceramics, subtransparent ceramics, optical properties, refractive index dispersion, Cauchy model

© 2014 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
lead-free ceramics, subtransparent ceramics, optical properties, refractive index dispersion, Cauchy model