<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>Pure and cobalt doped (x = 0.05, 0.10, 0.15 mol %) polycrystalline potassium hexatitanate (K2Ti6O13) ceramics were synthesized using conventional solid state reaction route. XRD result confirmed the successful doping of Co in the K2Ti6O13 matrix, as no additional peak was observed in the pattern. Dielectric permittivity was found to decrease with the increase in frequency while it increased with the increase in doping. The dielectric loss decreased with small doping whereas excessive doping caused its augmentation. Ac conductivity (σac) has also been studied as a function of frequency at room temperature for all the samples. Scanning Electron Microscope (SEM) inspection of the synthesized samples showed the formation of rod like shapes. FTIR analysis was carried out to identify the chemical bonds present in the system.</p></abstract>

Pure and cobalt doped (x = 0.05, 0.10, 0.15 mol %) polycrystalline potassium hexatitanate (K2Ti6O13) ceramics were synthesized using conventional solid state reaction route. XRD result confirmed the successful doping of Co in the K2Ti6O13 matrix, as no additional peak was observed in the pattern. Dielectric permittivity was found to decrease with the increase in frequency while it increased with the increase in doping. The dielectric loss decreased with small doping whereas excessive doping caused its augmentation. Ac conductivity (σac) has also been studied as a function of frequency at room temperature for all the samples. Scanning Electron Microscope (SEM) inspection of the synthesized samples showed the formation of rod like shapes. FTIR analysis was carried out to identify the chemical bonds present in the system.

Dielectric and spectroscopic analysis of cobalt doped potassium hexatitanate (K2Ti6O13) ceramics

Department of Physics, Integral University, Kursi Road, Lucknow, 226026, UP, India

Centre of Excellence in Material Science (Nanomaterials), Department of Applied Physics, Aligarh Muslim University, Aligarh, 202002, UP, India

Centre of Nanotechnology, King Abdulaziz University, Jeddah, Saudi Arabia

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Pure and cobalt doped (x = 0.05, 0.10, 0.15 mol %) polycrystalline potassium hexatitanate (K2Ti6O13) ceramics were synthesized using conventional solid state...

Dielectric and spectroscopic analysis of cobalt doped potassium hexatitanate (K2Ti6O13) ceramics

Pubblicato online: 15 dic 2013

Pagine: 555 - 560

DOI: https://doi.org/10.2478/s13536-013-0139-z

Parole chiave
ceramics, X-ray diffraction, dielectric properties, infrared spectroscopy

© 2013 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Dielectric and spectroscopic analysis of cobalt doped potassium hexatitanate (K2Ti6O13) ceramics

Pubblicato online: 15 dic 2013

Pagine: 555 - 560

DOI: https://doi.org/10.2478/s13536-013-0139-z

Parole chiaveceramics, X-ray diffraction, dielectric properties, infrared spectroscopy

© 2013 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
ceramics, X-ray diffraction, dielectric properties, infrared spectroscopy