<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>Superior electrical properties of carbon nanotubes were utilized by the authors in the fabrication of printed resistors. In common applications such as electrodes or sensors, only basic electrical and mechanical properties are investigated, leaving aside other key parameters related to the stability and reliability of particular elements. In this paper we present experimental results on the properties of printed resistive layers. One of the most important issues is their stability under high currents creating excessive thermal stresses. In order to investigate such behavior, a high direct current stress test was performed along with the observation of temperature distribution that allowed us to gain a fundamental insight into the electrical behavior at such operating conditions. These experiments allowed us to observe parametric failure or catastrophic damage that occurred under excessive supply parameters. Electrical parameters of all investigated samples remained stable after applying currents inducing an increase in temperature up to 130 °C and 200 °C. For selected samples, catastrophic failure was observed at the current values inducing temperature above 220 °C and 300 °C but in all cases the failure was related to the damage of PET or alumina substrate. Additional experiments were carried out with short high voltage pulse stresses. Printed resistors filled with nanomaterials sustained similar voltage levels (up to 750 V) without changing their parameters, while commonly used graphite filled polymer resistors changed their resistance value.</p></abstract>

Superior electrical properties of carbon nanotubes were utilized by the authors in the fabrication of printed resistors. In common applications such as electrodes or sensors, only basic electrical and mechanical properties are investigated, leaving aside other key parameters related to the stability and reliability of particular elements. In this paper we present experimental results on the properties of printed resistive layers. One of the most important issues is their stability under high currents creating excessive thermal stresses. In order to investigate such behavior, a high direct current stress test was performed along with the observation of temperature distribution that allowed us to gain a fundamental insight into the electrical behavior at such operating conditions. These experiments allowed us to observe parametric failure or catastrophic damage that occurred under excessive supply parameters. Electrical parameters of all investigated samples remained stable after applying currents inducing an increase in temperature up to 130 °C and 200 °C. For selected samples, catastrophic failure was observed at the current values inducing temperature above 220 °C and 300 °C but in all cases the failure was related to the damage of PET or alumina substrate. Additional experiments were carried out with short high voltage pulse stresses. Printed resistors filled with nanomaterials sustained similar voltage levels (up to 750 V) without changing their parameters, while commonly used graphite filled polymer resistors changed their resistance value.

Influence of electrical stress on printed polymer resistors filled with carbon nanomaterials

Institute of Metrology and Biomedical Engineering, Warsaw University of Technology, Św. A. Boboli 8, 02-525, Warsaw, Poland

Industrial Research Institute for Automation and Measurements, Al. Jerozolimskie 202, 02-486, Warsaw, Poland

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Superior electrical properties of carbon nanotubes were utilized by the authors in the fabrication of printed resistors. In common applications such as...

Influence of electrical stress on printed polymer resistors filled with carbon nanomaterials

Pubblicato online: 15 dic 2013

Pagine: 548 - 554

DOI: https://doi.org/10.2478/s13536-013-0131-7

Parole chiave
carbon nanotubes, printed electronics, polymer resistors, high current stress

© 2013 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Influence of electrical stress on printed polymer resistors filled with carbon nanomaterials

Pubblicato online: 15 dic 2013

Pagine: 548 - 554

DOI: https://doi.org/10.2478/s13536-013-0131-7

Parole chiavecarbon nanotubes, printed electronics, polymer resistors, high current stress

© 2013 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
carbon nanotubes, printed electronics, polymer resistors, high current stress