Protective layers of zirconium alloys used for claddings to improve the corrosion resistance

Bożena Sartowska

Bożena Sartowska

Institute of Nuclear Chemistry and TechnologyWarsaw, Poland
Profilo Orcid
Cerca questo autore su
Sciendo|Google Scholar
Sartowska, Bożena
, 
Wojciech Starosta

Wojciech Starosta

Institute of Nuclear Chemistry and TechnologyWarsaw, Poland
Profilo Orcid
Cerca questo autore su
Sciendo|Google Scholar
Starosta, Wojciech
, 
Paweł Sokołowski

Paweł Sokołowski

Wrocław University of Science and TechnologyWrocław, Poland
Cerca questo autore su
Sciendo|Google Scholar
Sokołowski, Paweł
, 
Danuta Wawszczak

Danuta Wawszczak

Institute of Nuclear Chemistry and TechnologyWarsaw, Poland
Cerca questo autore su
Sciendo|Google Scholar
Wawszczak, Danuta
 e 
Jerzy Smolik

Jerzy Smolik

Łukasiewicz Research Network – The Institute for Sustainable TechnologiesRadom, Poland
Profilo Orcid
Cerca questo autore su
Sciendo|Google Scholar
Smolik, Jerzy
  
25 giu 2024
Protective layers of zirconium alloys used for claddings to improve the corrosion resistance's Cover Image
INFORMAZIONI SU QUESTO ARTICOLO
Articolo precedente
Articolo Successivo
Cita
Scarica la copertina
Categoria dell'articolo: Original Paper
Pubblicato online: 25 giu 2024
Pagine: 125 - 128
Ricevuto: 05 ott 2023
Accettato: 12 mar 2024
DOI: https://doi.org/10.2478/nuka-2024-0018
Parole chiave
© 2024 Bożena Sartowska et al., published by Sciendo
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Fig. 1.

Physical vapor deposition ZrSi2 + Cr modified Zry-2 surface (a) SEM image X 10 000, (b) cross-section, (c) homogeneity of the Zr–Si–Cr coatings (wt%) at nine areas of the modified Zry-2.
Physical vapor deposition ZrSi2 + Cr modified Zry-2 surface (a) SEM image X 10 000, (b) cross-section, (c) homogeneity of the Zr–Si–Cr coatings (wt%) at nine areas of the modified Zry-2.

Fig. 2.

SEM images with X 10 000× magnification of the material surfaces after 63 days oxidation test (a) Zry-2 and (b) Zry-2 coated with Zr40Si24Cr36, (c) mass changes of Zry-2 and Zry-2 coated with Zr40Si24Cr36.
SEM images with X 10 000× magnification of the material surfaces after 63 days oxidation test (a) Zry-2 and (b) Zry-2 coated with Zr40Si24Cr36, (c) mass changes of Zry-2 and Zry-2 coated with Zr40Si24Cr36.

Fig. 3.

SEM images of the coated SiC grains presented with different magnifications: (a) 50 000×, (b) 100 000×, and (c) obtained elemental composition of the material.
SEM images of the coated SiC grains presented with different magnifications: (a) 50 000×, (b) 100 000×, and (c) obtained elemental composition of the material.