<p>Calcium-alumina-silicate-hydrate (C-A-S-H) is the main hydration product formed in Portland composite cement pastes. C-A-S-H is a key phase with regard to the strength and durability of concrete. Proper characterization of C-A-S-H is difficult due to intermixing with other phases, thus limiting the applicability of point scan analyses using scanning electron microscopy (SEM). Recent advances have enabled the use of hypermaps from energy dispersive spectroscopy (EDS) to investigate hydrate phases with better statistics. This study investigated how increased curing temperature and the inclusion of pozzolanic SCMs change the composition of the C-A-S-H, using the edxia plugin and SEM-EDS hypermaps. Composite cement pastes were cured at 20, 38, and 60°C for 180 days before analysis. We discuss the interpretation of the data from hypermaps in comparison to the traditional point scan approach.</p>
</abstract>

Calcium-alumina-silicate-hydrate (C-A-S-H) is the main hydration product formed in Portland composite cement pastes. C-A-S-H is a key phase with regard to the strength and durability of concrete. Proper characterization of C-A-S-H is difficult due to intermixing with other phases, thus limiting the applicability of point scan analyses using scanning electron microscopy (SEM). Recent advances have enabled the use of hypermaps from energy dispersive spectroscopy (EDS) to investigate hydrate phases with better statistics. This study investigated how increased curing temperature and the inclusion of pozzolanic SCMs change the composition of the C-A-S-H, using the edxia plugin and SEM-EDS hypermaps. Composite cement pastes were cured at 20, 38, and 60°C for 180 days before analysis. We discuss the interpretation of the data from hypermaps in comparison to the traditional point scan approach.

Determining the Influence of Curing Temperature and SCMs on C-A-S-H Composition Using SEM-EDS Hypermaps

Nordic Concrete Research

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Calcium-alumina-silicate-hydrate (C-A-S-H) is the main hydration product formed in Portland composite cement pastes. C-A-S-H is a key phase with regard to the...

Determining the Influence of Curing Temperature and SCMs on C-A-S-H Composition Using SEM-EDS Hypermaps

Pubblicato online: 05 lug 2024

Pagine: 125 - 146

Ricevuto: 02 apr 2024

Accettato: 24 giu 2024

DOI: https://doi.org/10.2478/ncr-2024-0006

Parole chiave
SEM-EDS, characterization, C-S-H, SCM, fly ash, volcanic pozzolana

© 2024 Petter Hemstad et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Determining the Influence of Curing Temperature and SCMs on C-A-S-H Composition Using SEM-EDS Hypermaps

Pubblicato online: 05 lug 2024

Pagine: 125 - 146

Ricevuto: 02 apr 2024

Accettato: 24 giu 2024

DOI: https://doi.org/10.2478/ncr-2024-0006

Parole chiaveSEM-EDS, characterization, C-S-H, SCM, fly ash, volcanic pozzolana

© 2024 Petter Hemstad et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
SEM-EDS, characterization, C-S-H, SCM, fly ash, volcanic pozzolana