Login
Registrati
Reimposta password
Pubblica & Distribuisci
Soluzioni Editoriali
Soluzioni di Distribuzione
Temi
Architettura e design
Arti
Business e Economia
Chimica
Chimica industriale
Farmacia
Filosofia
Fisica
Geoscienze
Ingegneria
Interesse generale
Legge
Letteratura
Linguistica e semiotica
Matematica
Medicina
Musica
Scienze bibliotecarie e dell'informazione, studi library
Scienze dei materiali
Scienze della vita
Scienze informatiche
Scienze sociali
Sport e tempo libero
Storia
Studi classici e del Vicino Oriente antico
Studi culturali
Studi ebraici
Teologia e religione
Pubblicazioni
Riviste
Libri
Atti
Editori
Blog
Contatti
Cerca
EUR
USD
GBP
Italiano
English
Deutsch
Polski
Español
Français
Italiano
Carrello
Home
Riviste
Materials Science-Poland
Volume 39 (2021): Numero 2 (June 2021)
Accesso libero
Synthetic alkaline-earth hydroxyapatites: Influence of their structural, textural, and morphological properties over Co
2+
ion adsorption capacity
Francisco Granados-Correa
Francisco Granados-Correa
e
Juan Bonifacio-Martínez
Juan Bonifacio-Martínez
| 10 nov 2021
Materials Science-Poland
Volume 39 (2021): Numero 2 (June 2021)
INFORMAZIONI SU QUESTO ARTICOLO
Articolo precedente
Articolo Successivo
Sommario
Articolo
Immagini e tabelle
Bibliografia
Autori
Articoli in questo Numero
Anteprima
PDF
Cita
CONDIVIDI
Pubblicato online:
10 nov 2021
Pagine:
252 - 264
Ricevuto:
19 mag 2021
Accettato:
20 set 2021
DOI:
https://doi.org/10.2478/msp-2021-0022
Parole chiave
barium hydroxyapatite
,
strontium hydroxyapatite
,
calcium hydroxyapatite
,
chemical precipitation synthesis
,
Co ion adsorption
© 2021 Francisco Granados-Correa et al., published by Sciendo
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Fig. 1
Chemical distribution of cobalt ionic species in aqueous media as a function of pH.
Fig. 2
XRD patterns of synthesized alkaline-earth hydroxyapatite powders prepared via chemical precipitation method followed by calcination at 1,100°C: (A) Ba-HAp, (B) Sr-HAp, and (C) Ca-HAp. Ba-HAp, barium hydroxyapatite; Ca-HAp, calcium hydroxyapatite; Sr-HAp, strontium hydroxyapatite.
Fig. 3
N2 adsorption-desorption isotherms of (A) Ba-HAp, (B) Sr-HAp, and (C) Ca-HAp powders. Ba-HAp, barium hydroxyapatite, Ca-HAp, calcium hydroxyapatite; Sr-HAp, strontium hydroxyapatite.
Fig. 4
SEM micrographs at 5,000 × and EDXS analysis of (A) Ba-HAp, (B) Sr-HAp, and (C) Ca-HAp powders. Ba-HAp, barium hydroxyapatite; Ca-HAp, calcium hydroxyapatite; Sr-HAp, strontium hydroxyapatite.
Fig. 5
FTIR spectrum of (A) Ba-HAp, (B) Sr-HAp, and (C) Ca-HAp powders. Ba-HAp, barium hydroxyapatite; Ca-HAp, calcium hydroxyapatite; Sr-HAp, strontium hydroxyapatite.
Textural characteristics of synthesized alkaline-earth hydroxyapatite materials and Co2+ ion adsorption capacities in percentage.
Sample
S
BET
(m
2
g
−1
)
a
V
t
(cm
3
g
−1
)
b
d
p
(nm)
c
Co
2+
ion adsorption capacity (%)
Ba-HAp
0.5216
0.0011
8.9231
6.03 ± 0.39
Sr-HAp
1.3874
0.0057
16.5310
17.46 ± 0.79
Ca-HAp
59.7000
0.1120
7.5046
56.84 ± 1.08