Effect of titanium source and sol-gel TiO₂ thin film formation parameters on its morphology and photocatalytic activity

TiO₂ thin films with different surface structure have been prepared from alkoxide solutions by the sol-gel method using different cationic precursors and heat treatment techniques. The effect of using titanium isopropoxide as well as titanium butoxide as a titanium source on the surface structure and photocatalytic activity of the resultant thin films was studied. Significant differences in the rate of hydrolysis and condensation reactions during the sol-gel synthesis were observed for these titanium precursors. This had a direct influence on the morphology of the as-prepared TiO₂ films. Higher quality oxide coatings were obtained from titanium isopropoxide. They were characterized by a smaller grain size, improved surface roughness and uniform coverage of the glass substrate. A beneficial effect of calcination process after each sol application cycle in contrast to single step calcination after all dip-coating cycles was observed. Photocatalytic degradation tests showed that methyl orange was decolorized in the presence of all prepared TiO₂ films by exposing their aqueous solutions to UV light (λ = 254 nm). The highest photocatalytic activity had the TiO₂ layer produced using titanium isopropoxide.