Thick film technique is popular because of low cost, simple for construction and better sensing surface area, hence for resistive gas sensor thick films of pure ZrO2 powder were prepared by Standard screen printing technique. The material was characterized by X-Ray diffraction pattern, surface morphology was observed by SEM, elemental composition were observed by EDAX and optical properties were studied with UV spectroscopy Techniques, electrical properties were studying with different applied voltages and at different working temperature. X-Ray Diffraction studies confirmed that the combinations of tetragonal and monoclinic structure. The energy band gap and the thicknesses of the films were evaluated, the crystalline grain size was determined using Scherrer’s formula. The gas sensing performances of various gases were tested with working temperatures from 100° to 500°c. The sensitivity and selectivity to different gases was tested and the resistive thick films showed highest response to NH3 (100 ppm) at 300°c. It was observed that increase in gas concentration its sensing response goes on increasing but slowly increase being still constant for higher concentration. The sensitivity and selectivity may be further enhanced by doping other element and ZrO2 can be stabilize by mixing other oxides. The quick response and fast recovery time was recorded.
</abstract>

Thick film technique is popular because of low cost, simple for construction and better sensing surface area, hence for resistive gas sensor thick films of pure ZrO2 powder were prepared by Standard screen printing technique. The material was characterized by X-Ray diffraction pattern, surface morphology was observed by SEM, elemental composition were observed by EDAX and optical properties were studied with UV spectroscopy Techniques, electrical properties were studying with different applied voltages and at different working temperature. X-Ray Diffraction studies confirmed that the combinations of tetragonal and monoclinic structure. The energy band gap and the thicknesses of the films were evaluated, the crystalline grain size was determined using Scherrer’s formula. The gas sensing performances of various gases were tested with working temperatures from 100° to 500°c. The sensitivity and selectivity to different gases was tested and the resistive thick films showed highest response to NH3 (100 ppm) at 300°c. It was observed that increase in gas concentration its sensing response goes on increasing but slowly increase being still constant for higher concentration. The sensitivity and selectivity may be further enhanced by doping other element and ZrO2 can be stabilize by mixing other oxides. The quick response and fast recovery time was recorded.

Preparation and Characterization of Zirconia Based Thick Film Resistor as a Ammonia Gas Sensor

International Journal on Smart Sensing and Intelligent Systems

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Thick film technique is popular because of low cost, simple for construction and better sensing surface area, hence for resistive gas sensor thick films of...

Preparation and Characterization of Zirconia Based Thick Film Resistor as a Ammonia Gas Sensor

Pubblicato online: 01 set 2012

Pagine: 540 - 558

Accettato: 23 ago 2012

DOI: https://doi.org/10.21307/ijssis-2017-494

© 2012 S. B. Deshmukh et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.