<abstract xmlns="http://www.w3.org/1999/xhtml">In this work, highly ordered porous anodic alumina (PAA) with tapered pore structure and interpore distance (Dc) in the range of 550 nm to 650 nm were fabricated. To produce hexagonal close-packed pore structure a two-step process, combining anodization in etidronic acid electrolyte in the first step and high-concentration, high-temperature anodization in citric acid electrolyte in the second step, was applied. The Al pre-patterned surface obtained in the first anodization was used to produce regular tapered pore arrays by subsequent and alternating anodization in 20 wt.% citric acid solution and pore wall etching in 10 wt.% phosphoric acid solution. The height of the tapered pores was ranging between 2.5 μm and 8.0 μm for the PAA with Dc = 550 nm and Dc = 650 nm, respectively. The geometry of the obtained graded structure can be used for a production of efficient antireflective coatings operating in IR spectral region.</abstract>

In this work, highly ordered porous anodic alumina (PAA) with tapered pore structure and interpore distance (Dc) in the range of 550 nm to 650 nm were fabricated. To produce hexagonal close-packed pore structure a two-step process, combining anodization in etidronic acid electrolyte in the first step and high-concentration, high-temperature anodization in citric acid electrolyte in the second step, was applied. The Al pre-patterned surface obtained in the first anodization was used to produce regular tapered pore arrays by subsequent and alternating anodization in 20 wt.% citric acid solution and pore wall etching in 10 wt.% phosphoric acid solution. The height of the tapered pores was ranging between 2.5 μm and 8.0 μm for the PAA with Dc = 550 nm and Dc = 650 nm, respectively. The geometry of the obtained graded structure can be used for a production of efficient antireflective coatings operating in IR spectral region.

Manufacturing of highly ordered porous anodic alumina with conical pore shape and tunable interpore distance in the range of 550 nm to 650 nm

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

In this work, highly ordered porous anodic alumina (PAA) with tapered pore structure and interpore distance (Dc) in the range of 550 nm to 650 nm were...

Manufacturing of highly ordered porous anodic alumina with conical pore shape and tunable interpore distance in the range of 550 nm to 650 nm

Pubblicato online: 31 ott 2017

Pagine: 511 - 518

Ricevuto: 22 ott 2016

Accettato: 03 mag 2017

DOI: https://doi.org/10.1515/msp-2017-0058

Parole chiave
porous anodic alumina, guided anodization, citric acid, etidronic acid, tapered pores, AR coatings

© 2017

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Manufacturing of highly ordered porous anodic alumina with conical pore shape and tunable interpore distance in the range of 550 nm to 650 nm

Pubblicato online: 31 ott 2017

Pagine: 511 - 518

Ricevuto: 22 ott 2016

Accettato: 03 mag 2017

DOI: https://doi.org/10.1515/msp-2017-0058

Parole chiaveporous anodic alumina, guided anodization, citric acid, etidronic acid, tapered pores, AR coatings

© 2017

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Parole chiave
porous anodic alumina, guided anodization, citric acid, etidronic acid, tapered pores, AR coatings