Properties of spinels depend on their composition, method of preparation and sintering temperature [1]. Simplicity of the cubic spinel structure has attracted many researchers around the world to explore multi-facet functionality and applications of ferrites. Ferrites occupy an important place in almost every industry branch, from electronics and communications to medical industry, military to space technology [2]. Their structural simplicity allows easy tailoring of materials with desired electrical, thermal, optical and magnetic properties. MgCuZn ferrites are known for their high environmental stability, low magnetocrystalline anisotropy, low cost and easy handling when compared to their counterpart NiCuZn ferrites [ 3– 11]. DC electrical resistivity and thermoelectric power of ZnMgNd, NiCuMgZn, NiZnMgCo, MgZn, MgTi and Mg–Fe–O [ 12– 17] spinel systems have been reported by several researchers. However, similar studies on MgCuZn ferrite system are not available in literature. Slight deficiency of iron in the MgCuZn ferrites prevents Fe2+ ion formation and thereby decreases the conductivity of ferrites. The present study is aimed at investigating DC electrical resistivity and Seebeck coefficient in a series of Mg0.5−xCuxZn0.5Fe1.9O4−δ (x = 0, 0.1, 0.15, 0.2 and 0.25) ferrites for probable applications as core materials of transformer and high definition TV deflection yokes.
Reagent grade MgO, CuO, ZnO and Fe2O3 were taken in stoichiometric proportions and mixed in an agate mortar for 8 hours. The mixed oxide powder was pre-sintered at 800 °C for 4 hours. The samples were again ground for 10 hours and then sieved for uniform particle size. So obtained green powder was pressed into a pellet of 10 mm diameter and 2 mm height with PVA as a binder, using a uniaxial press. The green pellet was annealed at 1150 °C for 4 hours in a programmable furnace. The dense ferrites were polished to obtain a smooth surface and painted on either side with a silver paste for a good electrical contact. These samples were used for DC electrical conductivity and thermoelectric power studies. DC resistivity was measured by two probe technique using Keithley electrometer, model 6514, interfaced to a PC and electrical furnace. Electrical resistance was measured at 5 °C intervals from room temperature to 300 °C. Resistivity was calculated from the dimensions of the pellet and measured resistance. The thermo-emf measurement technique was reported in detail in our earlier publication [18]. The thermo-emf measurements were recorded from room temperature to 400 °C. Seebeck coefficient α was calculated from the formula:
where Vs is the thermo-emf generated and T2 – T1 is the temperature difference at the hot and cold junctions which was 10 °C in the present case. With the help of thermoelectric power studies and DC electrical conductivity measurements one can calculate the mobility of the carriers using the following equation in case of low mobility semiconductors, such as ferrites:
where e is the charge of electron and k is the Boltzmann constant.
Activation energies of the carriers were estimated from the plots of 1000/T versus lnµ according to the relation:
Typical X-ray diffraction patterns of the Mg0.5−xCuxZn0.5Fe1.9O4−δ shown in Fig. 1 confirm the single phase spinel structure formation. It is seen in Fig. 2 that DC electrical conductivity decreases with an increase in copper concentration in the series of the samples. The iron deficient series of the samples exhibits higher resistivity than their counterparts with stoichiometric iron content [19]. This suggests that during sintering, formation of Fe3+ to Fe2+ ions was minimized due to the shortage of iron. Materials for transformer cores or television deflection yokes should have high resistivity of the order ~109 Ω·m and more, which has been attained in the present work. Yue et al. [20] reported an increase in electrical conductivity with the addition of copper, which is contrary to the results obtained in the present work.
The DC conductivity versus the reciprocal temperature for the series of the samples in the temperature range of 30 °C to 300 °C is shown in Fig. 3. The conductivity varies from 5.56 × 10−9 Ω−1·cm−1 to 2.21 × 10−5 Ω−1·cm−1, 5.90 × 10−10 Ω−1·cm−1 to 2.91 × 10−5 Ω−1·cm−1, 8.86 × 10−9 Ω−1·cm−1 to 1.30 × 10−4 Ω−1·cm−1 and 8.87 × 10−10 Ω−1·cm−1 to 1.52 × 10−4 Ω−1·cm−1 with x = 0.1, 0.15, 0.2 and 0.25, respectively. The plots are linear for all the samples with a slope change in the range of 60 °C to 80 °C, in the vicinity of magnetic Curie transition temperature (Tc from 70 °C to 100 °C). The slope change in the graphs indicates that there are two regions of conductivity viz. low temperature (ferromagnetic) region I and high temperature (paramagnetic) region II. Similar slope change near Curie transition temperature in Arrhenius plots for DC conductivity was observed by Rezlescu et al. [ 9, 21] and it was attributed to the influence of ferromagnetic ordering on conduction mechanism. In principle, this is due to destruction of spontaneous magnetization and the change in additional charge carrier concentration in the neighborhood of Curie transition temperature. In ferrites, being magnetic semiconductors, conductivity in the low temperature region I is attributed to impurities and is extrinsic in nature. At high temperatures, the conductivity is intrinsic in nature and is due to electron hopping between
Activation energies from DC conductivity studies and mobility of Mg0.5−xCuxZn0.5Fe1.9O4−δ.
From DC conductivity | From mobility | |||
---|---|---|---|---|
Copper content | Region I | Region II | Region I | Region II |
x | ΔE1 [eV] | ΔE2 [eV] | ΔE1 [eV] | ΔE2 [eV] |
0.1 | 0.45 | 0.66 | 0.23 | 0.61 |
0.15 | 0.35 | 0.87 | 0.39 | 0.86 |
0.2 | 0.36 | 0.92 | 0.29 | 0.81 |
0.25 | 0.73 | 0.9 | 0.26 | 0.84 |
The variation of Seebeck coefficient with copper concentration is shown in Fig. 4. All the samples exhibit a negative Seebeck coefficient indicating that the majority charge carriers are electrons. As the copper content increases, the magnitude of thermoelectric power decreases and reaches saturation at higher content of copper. Fig. 5 shows the variation of Seebeck coefficient with temperature for the non-stoichiometric MgCuZn ferrite samples. An examination of Fig. 5 reveals that there is a maximum of Seebeck coefficient for every composition at a temperature Ts. The temperature at which the maximum is obtained in Seebeck coefficient has been designated as Seebeck coefficient transition temperature Ts by Reddy et al. [22] and Ravinder [23]. It may be pointed out here that Ts and Curie transition temperature Tc are different from each other. The author is of the opinion that these maxima obtained are due to the charge carrier redistribution taking place at these temperatures. Repeated thermoelectric power measurements on these samples showed that there is some type of ordering taking place inside these samples.
The temperature dependence of charge carriers mobility for the series of the samples is shown in Fig. 6. In the investigated temperature range all the samples exhibit two regions of conductivity. The activation energies were calculated from the plots of charge carriers mobility, log µ versus 1/T. The activation energies of all the samples are tabulated in Table 1.
The effect of ferromagnetic-paramagnetic transition could be observed even in mobility plots proportional to DC conduction. The low temperature region, where an extrinsic conduction is favoured, is shown as region I in Table 1. In this region, the conductivity is basically due to the impurities. The activation energies (ΔE2) in the region II (intrinsic region) are found to be greater than those of region I. Further, the activation energies (ΔE2), estimated from DC conductivity and mobility plots are in good agreement at high T (temperature) region. The activation energies (ΔE1, ΔE2) are greater than the ionization energies (Ei = 0.1 eV) of the donor and acceptor atoms, thus ruling out the band theory of conduction. Moreover, these energies are greater than the
Nonstoichiometric Mg0.5−xCuxZn0.5Fe1.9O4−δ compounds with x varying from 0 to 0.25 have been synthesized by conventional double sintering technique. X-ray diffraction patterns confirmed the single phase spinel structure. DC electrical conductivity increased with copper concentration and temperature. Conduction in these compounds was due to electron transfer between