<abstract xmlns="http://www.w3.org/1999/xhtml">In this study, the authors deposited silicon oxynitride films by Radio Frequency Plasma Enhanced Chemical Vapour Deposition (RF PECVD) method. The research explores the relationship between the deposition process parameters and the optical properties of the deposited SiOxNy films. The optical constants of SiOxNy films were measured and calculated by spectroscopic ellipsometry method. Additionally, the authors investigated the possibility of controlling the deposited film composition by the flow ratio of different gaseous precursors: ammonia (NH3), diluted silane (2%SiH4/98%N2), nitrous oxide (N2O) and nitrogen (N2). The gas mixture introduced to the working chamber during the growth of the film has the influence on the Si–O and Si–N bonds formation and the ratio between these bonds determines the refractive index of the deposited film.</abstract>

In this study, the authors deposited silicon oxynitride films by Radio Frequency Plasma Enhanced Chemical Vapour Deposition (RF PECVD) method. The research explores the relationship between the deposition process parameters and the optical properties of the deposited SiOxNy films. The optical constants of SiOxNy films were measured and calculated by spectroscopic ellipsometry method. Additionally, the authors investigated the possibility of controlling the deposited film composition by the flow ratio of different gaseous precursors: ammonia (NH3), diluted silane (2%SiH4/98%N2), nitrous oxide (N2O) and nitrogen (N2). The gas mixture introduced to the working chamber during the growth of the film has the influence on the Si–O and Si–N bonds formation and the ratio between these bonds determines the refractive index of the deposited film.

<div xmlns="http://www.w3.org/1999/xhtml"><sec id="j_msp-2016-0111_s_001_w2aab3b8d330b1b7b1ab1aAa"><label>1</label><div>Introduction</div>Silicon oxynitride (SiOxNy) films are a nonstoichiometric material with interesting properties. The SiOxNy films have diverse parameters, ranging from those of the silicon dioxide (SiO2) to the silicon nitride (Si3N4). The versatile properties of the films create many possibilities of application in different fields such as microelectronics [<a ref-type="bibr" href="#j_msp-2016-0111_ref_001_w2aab3b8d330b1b7b1ab2b1b1Aa">1</a>, <a ref-type="bibr" href="#j_msp-2016-0111_ref_002_w2aab3b8d330b1b7b1ab2b1b2Aa">2</a>], optoelectronics [<a ref-type="bibr" href="#j_msp-2016-0111_ref_003_w2aab3b8d330b1b7b1ab2b1b3Aa">3</a>, <a ref-type="bibr" href="#j_msp-2016-0111_ref_004_w2aab3b8d330b1b7b1ab2b1b4Aa">4</a>] or in micro-electro-mechanical systems (MEMS) technology [<a ref-type="bibr" href="#j_msp-2016-0111_ref_005_w2aab3b8d330b1b7b1ab2b1b5Aa">5</a>].Silicon compounds such as SiO2 and Si3N4 are widely applied dielectrics in microelectronics due to their adequate electrical, thermal and mechanical properties. However, SiO2 dielectric films have reached the technological limit as the properties of silicon dioxide are unsatisfactory for novel micro- and optoelectronic devices. Additionally, the silicon oxynitride films have better not only dielectric, but also optical properties. The optical losses in SiOxNy films are significantly lower and the refractive index of the films can be adjusted from 1.46 to around 2.1. Therefore, in the future silicon oxynitride can replace silicon dioxide in the semiconductor industry.In an earlier study, the authors have deposited Si3N4 films by Plasma Enhanced Chemical Vapour Deposition (PECVD) method and investigated their optical properties [<a ref-type="bibr" href="#j_msp-2016-0111_ref_006_w2aab3b8d330b1b7b1ab2b1b6Aa">6</a>].In this study, the conditions of the <bold>PECVD</bold> process were modified in order to manufacture SiOxNy films. The influence of the gas precursor flow rate on the optical parameters of the deposited films was investigated.</sec><sec id="j_msp-2016-0111_s_002_w2aab3b8d330b1b7b1ab1b1Aa"><label>2</label><div>Experimental method</div>The investigated silicon oxynitride films were deposited in a commercially available PlasmaLab 80Plus system manufactured by Oxford Instruments. The films were deposited on thermally oxidized p-type silicon (1 1 1) substrates (dSiO2 = 230 nm) in order to improve the quality of the manufactured SiOxNy films. The films were deposited using silane diluted in nitrogen (2% SiH4/98 % N2), ammonia (NH3) and nitrous oxide (N2O) as gaseous precursors. The duration of each deposition process was set at 5 minutes.In each deposition process the RF signal (13.56 MHz) was supplied to the upper electrode for capacitive plasma coupling and the forward power of the signal was set to 20 W. The pressure was controlled by the APC valve and was stabilized at 86.5 Pa while the temperature of the table with substrates was stabilized at 350 °C. The flow rates of 2 % SiH4/98 % N2 and N2O were set at 425 sccm and 350 sccm, respectively. The set value of NH3 flow rate was different for each deposition process, ranging from 10 to 50 sccm.The spectroscopic ellipsometry studies give information about the thickness and refractive index n value of the deposited SiOxNy film. The measurements were performed on a J. A. Woollam Co. ellipsometer that makes posible to carry out the measurements at different incidence angles (65°, 70°, 75°). The parameters were calculated for wavelength ranging from 300 to 1000 nm with the measurement resolution of 10 nm. The reflection coefficient of the SiOx<italic>N</italic>>y/SiO2 bilayer was measured in a system with integrating sphere.</sec><sec id="j_msp-2016-0111_s_003_w2aab3b8d330b1b7b1ab1b2Aa"><label>3</label><div>Results</div>The measurements were carried out in order to perform calibration of <bold>PECVD</bold> process and characterization of optical properties of the manufactured SiOxNy films. From the measured thickness of the deposited film, the growth rate of the film was calculated. <a ref-type="fig" href="#j_msp-2016-0111_fig_001_w2aab3b8d330b1b7b1ab1b2b4Aa">Fig. 1</a> shows the correlation of the film growth rate with the flow rate of NH3 during the deposition process.From the analysis of the measured data it follows that the growth rate of the SiOxNy film is decreasing linearly with the increasing flow rate of NH3. The increase of the NH3 flow rate results in the increase of the nitrogen (ammonia) to oxygen radicals ratio. The active species (ions and radicals) are created by electron-impact ionization and dissociation of precursor gases and they determine the probability of Si-N and Si-O bonds formation. During the growth of the SiOxNy films deposited utilizing <bold>PECVD</bold> method, the most probable reaction is the formation of the Si-O bonds. The increase of the reactive species containing nitrogen results in the oxygen deficiency and formation of Si-N bonds [<a ref-type="bibr" href="#j_msp-2016-0111_ref_007_w2aab3b8d330b1b7b1ab2b1b7Aa">7</a>].<figure id="j_msp-2016-0111_fig_001_w2aab3b8d330b1b7b1ab1b2b4Aa" position="float" fig-type="figure"><h2></h2><figCaption>Growth rate of the SiOxNy film deposited by the PECVD technique as a function of ammonia flow rate.</figCaption><img xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="graphic/j_msp-2016-0111_fig_001.jpg" src="https://sciendo-parsed.s3.eu-central-1.amazonaws.com/647250b8215d2f6c89dc3e1a/j_msp-2016-0111_fig_001.jpg?X-Amz-Algorithm=AWS4-HMAC-SHA256&amp;X-Amz-Date=20240603T082508Z&amp;X-Amz-SignedHeaders=host&amp;X-Amz-Expires=18000&amp;X-Amz-Credential=AKIA6AP2G7AKP25APDM2%2F20240603%2Feu-central-1%2Fs3%2Faws4_request&amp;X-Amz-Signature=224476040136ba667725ce901e50757c8e6cf5d3735b2ad8b85f2a337336eb53" class="mw-100"/></figure>As it is known, the deposition rate of the SiO2 films manufactured by <bold>PECVD</bold> method is few times higher comparing to the deposition rate of Si3N4 films. Therefore, it could be expected that the increase of the NH3 flow rate will result in the lower growth rate of the SiOxNy film and higher concentration of nitrogen in the composition of the deposited film. The changes of the composition and bonding configuration of the deposited SiOxNy films should be verified by the X-ray photoelectron spectroscopy investigation.The changes in the composition of SiOxNy have an influence on the optical properties of the deposited film. The ellipsometric studies showed that the refractive index of the SiOxNy films was increasing with the flow rate of NH3. In the investigated range of the set NH3 flow rates values, the refractive index of the films was changing from 1.51 to 1.55. The values of the refractive index of the investigated SiOxNy films, measured for the spectral wavelength of 300 to 1000 nm, are presented in <a ref-type="fig" href="#j_msp-2016-0111_fig_002_w2aab3b8d330b1b7b1ab1b2b7Aa">Fig. 2</a>.<figure id="j_msp-2016-0111_fig_002_w2aab3b8d330b1b7b1ab1b2b7Aa" position="float" fig-type="figure"><h2></h2><figCaption>Refractive index as a function of wavelength for SiOxNy films deposited at different NH3 flow rates.</figCaption><img xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="graphic/j_msp-2016-0111_fig_002.jpg" src="https://sciendo-parsed.s3.eu-central-1.amazonaws.com/647250b8215d2f6c89dc3e1a/j_msp-2016-0111_fig_002.jpg?X-Amz-Algorithm=AWS4-HMAC-SHA256&amp;X-Amz-Date=20240603T082508Z&amp;X-Amz-SignedHeaders=host&amp;X-Amz-Expires=18000&amp;X-Amz-Credential=AKIA6AP2G7AKP25APDM2%2F20240603%2Feu-central-1%2Fs3%2Faws4_request&amp;X-Amz-Signature=fdb1e4f7e2e41c33370fa7a7389c6ac876f9987bd13e71aa7be7cb9a773f4a57" class="mw-100"/></figure>The values of the refractive indexes of the investigated SiOxNy films are close to the value specific for silicon dioxide. Therefore, it means that in the bonding configuration of the deposited films, the Si-O bonds are dominant. From the analysis of the acquired measured data it follows that the refractive index of the deposited SiOxNy films can be precisely controlled by the NH3 flow rate. The refractive index and composition of the SiOxNy films are mainly influenced by the ratio between SiH4/N2O flow rates. Reduction of the N2O flow rate should result in growth of the films with higher refractive index.The refractive index of silicon oxynitride can be modified in a wide range from 1.46 to 2.1. The possibility creates many application solutions of the films in the technology of micro- and optoelectronic devices. The investigated films also have very low extinction coefficient value (k), lower than the sensitivity of the ellipsometer applied for the measurements (k &lt; 10 -7).To investigate the applicability of the SiOxNy films for antireflective coatings, the reflection coefficient of the SiOxNy films deposited on SiO2 buffer layer was measured. The value of the reflection coefficient from the SiOxNy/SiO2 bilayer was measured for wavelengths ranging from 250 to 1000 nm <a ref-type="fig" href="#j_msp-2016-0111_fig_003_w2aab3b8d330b1b7b1ab1b2c11Aa">(Fig. 3)</a>. The measurements were carried out in a system with the integrating sphere in order to improve the detectability of the light that was scattered or reflected by the surface roughness, SiOxNy/SiO2 interface or material inhomogeneity. Therefore, the measured value of the reflection coefficient is more accurate.<figure id="j_msp-2016-0111_fig_003_w2aab3b8d330b1b7b1ab1b2c11Aa" position="float" fig-type="figure"><h2></h2><figCaption>Comparison of reflection coefficients of the Si substrate, SiO2 buffer and SiO2/SiON bilayer.</figCaption><img xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="graphic/j_msp-2016-0111_fig_003.jpg" src="https://sciendo-parsed.s3.eu-central-1.amazonaws.com/647250b8215d2f6c89dc3e1a/j_msp-2016-0111_fig_003.jpg?X-Amz-Algorithm=AWS4-HMAC-SHA256&amp;X-Amz-Date=20240603T082508Z&amp;X-Amz-SignedHeaders=host&amp;X-Amz-Expires=18000&amp;X-Amz-Credential=AKIA6AP2G7AKP25APDM2%2F20240603%2Feu-central-1%2Fs3%2Faws4_request&amp;X-Amz-Signature=8839173b2f097c43d4968f941b8983c53e4f2ff2b3b117a11c9e47c1fb72b7c1" class="mw-100"/></figure>In the measured spectra, oscillation of the reflection coefficient value is observed. The oscillations are present due to the interference of the incident radiation and the radiation reflected from the interfaces of different materials. The number and locations of the peaks are dependent on the number of interfaces, thickness of the layers and construction of the antireflection coating. The investigated bilayers of SiOxNy/SiO2 (~250/230 nm) films are thicker comparing with the Si3N4 and Nb2O5 (~60 nm) or TiO2/SiO2 (~10-130/40-60 nm) multilayer antireflection coatings [<a ref-type="bibr" href="#j_msp-2016-0111_ref_008_w2aab3b8d330b1b7b1ab2b1b8Aa">8</a>-<a ref-type="bibr" href="#j_msp-2016-0111_ref_010_w2aab3b8d330b1b7b1ab2b1c10Aa">10</a>]. Due to the fact, the number of oscillations in the measured spectra is higher than normally and can be reduced by the decrease and optimization of the thickness of the deposited films.From the measured data it follows that the investigated SiOxNy films can be applied as antireflective coatings. It is possible to precisely control the value of the refractive index of the SiOxNy in a wide range of values by the deposition process parameters. The mentioned advantage of the investigated films makes them interesting in the design of optical layers, because it is possible to adjust the refractive index of the film to a specific material system (i.e. silicon or AIIIBV semiconductor compounds).</sec><sec id="j_msp-2016-0111_s_004_w2aab3b8d330b1b7b1ab1b3Aa"><label>4</label><div>Conclusions</div>The silicon oxynitride films were deposited by PECVD method on oxidized silicon substrates. The flow rate of the NH3 during the growth of the film was modified in each deposition process in order to obtain films with different Si-O and Si-N bonding fractions. The optical properties of the SiOxNy films were investigated using spectroscopic ellipsometry. Additionally, the bilayer consisting of SiOxNy and SiO2 was measured as an antireflective coating.The study showed that the properties of the deposited SiOxNy film can be modified and controlled by the flow rates of the gaseous precursors. The value of the refractive index of the deposited film can be controlled, so it is possible to obtain films with specified optical properties. Moreover, the deposited films have been found to be of very good optical quality. The value of the extinction coefficient of the investigated films was lower than the sensitivity of the applied ellipsometer. Therefore, the SiOxNy films manufactured by <bold>PECVD</bold> technique can be successfully used for optoelectronic and photonic applications such as antireflective coatings, optical filters or waveguide layers.The future works will concern the application of silicon dioxide, silicon nitride and silicon oxynitride in the technology of micro- and optoelectronic structures (Bragg reflectors, optical filters and antireflective layers for photovoltaic cells, LEDs and photodetectors).</sec></div>

Investigation of optical properties of silicon oxynitride films deposited by RF PECVD method

Division of Microelectronics and Nanotechnology, Faculty of Microsystem Electronics and Photonics, Wrocław University of Science and Technology, Janiszewskiego 11/17, 50-372 Wrocław,

Division of Microsystems and Photonics, Faculty of Microsystem Electronics and Photonics, Wrocław University of Science and Technology, Janiszewskiego 11/17, 50-372 Wrocław

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

In this study, the authors deposited silicon oxynitride films by Radio Frequency Plasma Enhanced Chemical Vapour Deposition (RF PECVD) method. The research...

Investigation of optical properties of silicon oxynitride films deposited by RF PECVD method

Pubblicato online: 27 nov 2016

Pagine: 868 - 871

Ricevuto: 20 apr 2016

Accettato: 26 set 2016

DOI: https://doi.org/10.1515/msp-2016-0111

Parole chiave
silicon oxynitride, RF PECVD, spectroscopic ellipsometry, reflection coefficient

© Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Investigation of optical properties of silicon oxynitride films deposited by RF PECVD method

Pubblicato online: 27 nov 2016

Pagine: 868 - 871

Ricevuto: 20 apr 2016

Accettato: 26 set 2016

DOI: https://doi.org/10.1515/msp-2016-0111

Parole chiavesilicon oxynitride, RF PECVD, spectroscopic ellipsometry, reflection coefficient

© Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
silicon oxynitride, RF PECVD, spectroscopic ellipsometry, reflection coefficient