<abstract xmlns="http://www.w3.org/1999/xhtml">In this paper, the impact of partial substitution of calcium for barium in (Ba1-xCax) (M0.9Y0.1) O3, M = Ce, Zr on physicochemical properties of the powders and sintered samples was investigated. The powders, with various contents of calcium (x = 0, 0.02, 0.05, 0.1), were prepared by means of thermal decomposition of organometallic precursors containing EDTA. All of the BaCeO3-based powders synthesised at 1100 °C were monophasic with a rhombohedral structure, however, completely cubic BaZrO3-based solid solutions were obtained at 1200 °C. A study of the sinterability of BaZr0.9Y0.1O3 and BaCe0.9Y0.1O3-based pellets was performed under non-isothermal conditions within a temperature range of 25 to 1200 °C. The partial substitution of barium for calcium in the (Ba1-xCax) (M0.9Y0.1) O3, M = Ce, Zr solid solution improved the sinterability of the samples in comparison to the initial BaCe0.9Y0.1O3 or BaZr0.9Y0.1O3. The relative density of calcium-modified BaCe0.9Y0.1O3-based samples reached approximately 95 to 97 % after sintering at 1500 °C for 2 h in air. The same level of relative density was achieved after sintering calcium-modified BaZr0.9Y0.1O3 at 1600 °C for 2 h. Analysis of the electrical conductivity from both series of investigated materials showed that the highest ionic conductivity, in air and wet 5 % H2 in Ar, was attained for the compositions of x = 0.02 to 0.05 (Ba1-xCax)(M0.9Y0.1)O3, M = Zr, Ce. The oxygen reduction reaction on the interface Pt│BaM0.9Y0.1O3, M = Ce, Zr was investigated using Pt microelectrodes. Selected samples of (Ba1-xCax) (M0.9Y0.1)O3, M = Zr, Ce were tested as ceramic electrolytes in hydrogen-oxygen solid oxide fuel cells operating at temperatures of 700 to 850 °C.</abstract>

In this paper, the impact of partial substitution of calcium for barium in (Ba1-xCax) (M0.9Y0.1) O3, M = Ce, Zr on physicochemical properties of the powders and sintered samples was investigated. The powders, with various contents of calcium (x = 0, 0.02, 0.05, 0.1), were prepared by means of thermal decomposition of organometallic precursors containing EDTA. All of the BaCeO3-based powders synthesised at 1100 °C were monophasic with a rhombohedral structure, however, completely cubic BaZrO3-based solid solutions were obtained at 1200 °C. A study of the sinterability of BaZr0.9Y0.1O3 and BaCe0.9Y0.1O3-based pellets was performed under non-isothermal conditions within a temperature range of 25 to 1200 °C. The partial substitution of barium for calcium in the (Ba1-xCax) (M0.9Y0.1) O3, M = Ce, Zr solid solution improved the sinterability of the samples in comparison to the initial BaCe0.9Y0.1O3 or BaZr0.9Y0.1O3. The relative density of calcium-modified BaCe0.9Y0.1O3-based samples reached approximately 95 to 97 % after sintering at 1500 °C for 2 h in air. The same level of relative density was achieved after sintering calcium-modified BaZr0.9Y0.1O3 at 1600 °C for 2 h. Analysis of the electrical conductivity from both series of investigated materials showed that the highest ionic conductivity, in air and wet 5 % H2 in Ar, was attained for the compositions of x = 0.02 to 0.05 (Ba1-xCax)(M0.9Y0.1)O3, M = Zr, Ce. The oxygen reduction reaction on the interface Pt│BaM0.9Y0.1O3, M = Ce, Zr was investigated using Pt microelectrodes. Selected samples of (Ba1-xCax) (M0.9Y0.1)O3, M = Zr, Ce were tested as ceramic electrolytes in hydrogen-oxygen solid oxide fuel cells operating at temperatures of 700 to 850 °C.

Some observations on the synthesis and electrolytic properties of (Ba1-xCax) (M0.9Y0.1)O3, M = Ce, Zr-based samples modified with calcium

AGH University of Science and Technology, Faculty of Fuels and Energy, al.Mickiewicza 30, 30–059 Cracow,

AGH University of Science and Technology, Faculty of Materials Science and Ceramics, al. Mickiewicza 30, 30-059 Cracow,

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Some observations on the synthesis and electrolytic properties of (BaCa) (MY)O, M = Ce, Zr-based samples modified with calcium

In this paper, the impact of partial substitution of calcium for barium in (Ba1-xCax) (M0.9Y0.1) O3, M = Ce, Zr on physicochemical properties of the powders...

Some observations on the synthesis and electrolytic properties of (Ba_1-xCa_x) (M_0.9Y_0.1)O₃, M = Ce, Zr-based samples modified with calcium

Article Category: Research Article

Pubblicato online: 27 apr 2016

Pagine: 101 - 114

Ricevuto: 07 lug 2015

Accettato: 11 dic 2015

DOI: https://doi.org/10.1515/msp-2016-0022

Parole chiave
ceramics, electrochemical measurements, ionic conductivity, IT-SOFC – intermediate temperature solid oxide fuelcell

© 2016 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Some observations on the synthesis and electrolytic properties of (Ba1-xCax) (M0.9Y0.1)O3, M = Ce, Zr-based samples modified with calcium

Article Category: Research Article

Pubblicato online: 27 apr 2016

Pagine: 101 - 114

Ricevuto: 07 lug 2015

Accettato: 11 dic 2015

DOI: https://doi.org/10.1515/msp-2016-0022

Parole chiaveceramics, electrochemical measurements, ionic conductivity, IT-SOFC – intermediate temperature solid oxide fuelcell

© 2016 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Some observations on the synthesis and electrolytic properties of (Ba_1-xCa_x) (M_0.9Y_0.1)O₃, M = Ce, Zr-based samples modified with calcium

Parole chiave
ceramics, electrochemical measurements, ionic conductivity, IT-SOFC – intermediate temperature solid oxide fuelcell