<abstract xmlns="http://www.w3.org/1999/xhtml">SrO–Sb2O3–P2O5 glass system was prepared by high temperature melting method. The effects of Sb2O3 and P2O5 content on the structure, thermal behavior and chemical durability of the glasses were studied by infrared spectrometer, thermal dilatometer, differential thermal analyzer and constant temperature water bath heating. It can be concluded that the characteristic temperatures of the glasses increased firstly and then decreased with the increasing of Sb2O3 content, whereas the tendency of the coefficient of thermal expansion (CTE) varied inversely. The crystallization ability of the glasses was significantly increased and the water resistance was reduced for Sb2O3 content of 35 mol % and 40 mol %. The glasses with 20 mol %, 25 mol % and 30 mol % Sb2O3 showed better performance in every respect than the others and the glasses containing 25 mol % Sb2O3, characterized by the best performance, can be chosen as host glasses for further research.</abstract>

SrO–Sb2O3–P2O5 glass system was prepared by high temperature melting method. The effects of Sb2O3 and P2O5 content on the structure, thermal behavior and chemical durability of the glasses were studied by infrared spectrometer, thermal dilatometer, differential thermal analyzer and constant temperature water bath heating. It can be concluded that the characteristic temperatures of the glasses increased firstly and then decreased with the increasing of Sb2O3 content, whereas the tendency of the coefficient of thermal expansion (CTE) varied inversely. The crystallization ability of the glasses was significantly increased and the water resistance was reduced for Sb2O3 content of 35 mol % and 40 mol %. The glasses with 20 mol %, 25 mol % and 30 mol % Sb2O3 showed better performance in every respect than the others and the glasses containing 25 mol % Sb2O3, characterized by the best performance, can be chosen as host glasses for further research.

Influence of composition on the structure and properties of SrO–Sb2O3–P2O5 low-melting sealing glasses

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Influence of composition on the structure and properties of SrO–SbO–PO low-melting sealing glasses

SrO–Sb2O3–P2O5 glass system was prepared by high temperature melting method. The effects of Sb2O3 and P2O5 content on the structure, thermal behavior and...

Influence of composition on the structure and properties of SrO–Sb₂O₃–P₂O₅ low-melting sealing glasses

Pubblicato online: 06 gen 2016

Pagine: 862 - 866

Ricevuto: 08 mar 2015

Accettato: 06 ott 2015

DOI: https://doi.org/10.1515/msp-2015-0117

Parole chiave
thermal behavior, chemical durability, coefficient of thermal expansion, water durability

© 2015 Haining Nie et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Influence of composition on the structure and properties of SrO–Sb2O3–P2O5 low-melting sealing glasses

Pubblicato online: 06 gen 2016

Pagine: 862 - 866

Ricevuto: 08 mar 2015

Accettato: 06 ott 2015

DOI: https://doi.org/10.1515/msp-2015-0117

Parole chiavethermal behavior, chemical durability, coefficient of thermal expansion, water durability

© 2015 Haining Nie et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Influence of composition on the structure and properties of SrO–Sb₂O₃–P₂O₅ low-melting sealing glasses

Parole chiave
thermal behavior, chemical durability, coefficient of thermal expansion, water durability