<abstract xmlns="http://www.w3.org/1999/xhtml"><p>In this work, zinc oxide (ZnO) nanorods were obtained by a simple chemical precipitation method in the presence of capping agent: polyvinyl pyrrolidone (PVP) at room temperature. X-ray diffraction (XRD) result indicates that the synthesized undoped ZnO nanorods have hexagonal wurtzite structure without any impurities. It has been observed that the growth direction of the prepared ZnO nanorods is [1 0 1]. XRD analysis revealed that the nanorods have the crystallite size of 49 nm. Crystallite size is calculated by Debye-Scherrer formula and lattice strain is calculated by Williomson-Hall equation. Cell volume, Lorentz factor, Lorentz polarization factor, bond length, texture coefficient, lattice constants and dislocation density have also been studied. We also compared the interplanar spacings and relative peak intensities with their standard values at different angles. The scanning electron microscope (SEM) images confirmed the size and shape of these nanorods. It has been found that the diameter of the nanorods ranges from 1.52 μm to 1.61 μm and the length is about 4.89 μm. It has also been observed that at room temperature ultraviolet visible (UV-Vis) absorption band is around 355 nm (blue shifted as compared to the bulk). The average particle size has also been calculated by mathematical model of effective mass approximation equation, using UV-Vis absorption peak. Finally, the bandgap has been calculated using UV-absorption peak. Electroluminescence (EL) studies show that emission of light is possible at very small threshold voltage and it increases rapidly with increasing applied voltage. It is seen that smaller ZnO nanoparticles give higher electroluminescence brightness starting at lower threshold voltage. The brightness is also affected by increasing the frequency of AC signal.</p></abstract>

In this work, zinc oxide (ZnO) nanorods were obtained by a simple chemical precipitation method in the presence of capping agent: polyvinyl pyrrolidone (PVP) at room temperature. X-ray diffraction (XRD) result indicates that the synthesized undoped ZnO nanorods have hexagonal wurtzite structure without any impurities. It has been observed that the growth direction of the prepared ZnO nanorods is [1 0 1]. XRD analysis revealed that the nanorods have the crystallite size of 49 nm. Crystallite size is calculated by Debye-Scherrer formula and lattice strain is calculated by Williomson-Hall equation. Cell volume, Lorentz factor, Lorentz polarization factor, bond length, texture coefficient, lattice constants and dislocation density have also been studied. We also compared the interplanar spacings and relative peak intensities with their standard values at different angles. The scanning electron microscope (SEM) images confirmed the size and shape of these nanorods. It has been found that the diameter of the nanorods ranges from 1.52 μm to 1.61 μm and the length is about 4.89 μm. It has also been observed that at room temperature ultraviolet visible (UV-Vis) absorption band is around 355 nm (blue shifted as compared to the bulk). The average particle size has also been calculated by mathematical model of effective mass approximation equation, using UV-Vis absorption peak. Finally, the bandgap has been calculated using UV-absorption peak. Electroluminescence (EL) studies show that emission of light is possible at very small threshold voltage and it increases rapidly with increasing applied voltage. It is seen that smaller ZnO nanoparticles give higher electroluminescence brightness starting at lower threshold voltage. The brightness is also affected by increasing the frequency of AC signal.

Study of structural, morphological, optical and electroluminescent properties of undoped ZnO nanorods grown by a simple chemical precipitation

Department of Physics, Rungta College of Engineering and Technology

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

In this work, zinc oxide (ZnO) nanorods were obtained by a simple chemical precipitation method in the presence of capping agent: polyvinyl pyrrolidone (PVP)...

Study of structural, morphological, optical and electroluminescent properties of undoped ZnO nanorods grown by a simple chemical precipitation

Pubblicato online: 06 gen 2016

Pagine: 751 - 759

Ricevuto: 09 dic 2014

Accettato: 22 set 2015

DOI: https://doi.org/10.1515/msp-2015-0112

Parole chiave
electroluminescence, optoelectronics, nanomaterials, nanorods, zinc oxide

© 2015 A. Singh et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Study of structural, morphological, optical and electroluminescent properties of undoped ZnO nanorods grown by a simple chemical precipitation

Pubblicato online: 06 gen 2016

Pagine: 751 - 759

Ricevuto: 09 dic 2014

Accettato: 22 set 2015

DOI: https://doi.org/10.1515/msp-2015-0112

Parole chiaveelectroluminescence, optoelectronics, nanomaterials, nanorods, zinc oxide

© 2015 A. Singh et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
electroluminescence, optoelectronics, nanomaterials, nanorods, zinc oxide