<abstract xmlns="http://www.w3.org/1999/xhtml">Lithium manganese oxide thin films were deposited on sodalime glass substrates by metal organic chemical vapour deposition (MOCVD) technique. The films were prepared by pyrolysis of lithium manganese acetylacetonate precursor at a temperature of 420 °C with a flow rate of 2.5 dm3/min for two-hour deposition period. Rutherford backscattering spectroscopy (RBS), UV-Vis spectrophotometry, X-ray diffraction (XRD) spectroscopy, atomic force microscopy (AFM) and van der Pauw four point probe method were used for characterizations of the film samples. RBS studies of the films revealed fair thickness of 1112.311 (1015 atoms/cm2) and effective stoichiometric relationship of Li0.47Mn0.27O0.26. The films exhibited relatively high transmission (50 % T) in the visible and NIR range, with the bandgap energy of 2.55 eV. Broad and diffused X-ray diffraction patterns obtained showed that the film was amorphous in nature, while microstructural studies indicated dense and uniformly distributed layer across the substrate. Resistivity value of 4.9 Ω·cm was obtained for the thin film. Compared with Mn0.2O0.8 thin film, a significant lattice absorption edge shift was observed in the Li0.47Mn0.27O0.26 film.</abstract>

Lithium manganese oxide thin films were deposited on sodalime glass substrates by metal organic chemical vapour deposition (MOCVD) technique. The films were prepared by pyrolysis of lithium manganese acetylacetonate precursor at a temperature of 420 °C with a flow rate of 2.5 dm3/min for two-hour deposition period. Rutherford backscattering spectroscopy (RBS), UV-Vis spectrophotometry, X-ray diffraction (XRD) spectroscopy, atomic force microscopy (AFM) and van der Pauw four point probe method were used for characterizations of the film samples. RBS studies of the films revealed fair thickness of 1112.311 (1015 atoms/cm2) and effective stoichiometric relationship of Li0.47Mn0.27O0.26. The films exhibited relatively high transmission (50 % T) in the visible and NIR range, with the bandgap energy of 2.55 eV. Broad and diffused X-ray diffraction patterns obtained showed that the film was amorphous in nature, while microstructural studies indicated dense and uniformly distributed layer across the substrate. Resistivity value of 4.9 Ω·cm was obtained for the thin film. Compared with Mn0.2O0.8 thin film, a significant lattice absorption edge shift was observed in the Li0.47Mn0.27O0.26 film.

Metal-organic chemical vapour deposition of lithium manganese oxide thin films via single solid source precursor

University of KwaZulu Natal Pietermaritzburg

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Lithium manganese oxide thin films were deposited on sodalime glass substrates by metal organic chemical vapour deposition (MOCVD) technique. The films were...

Metal-organic chemical vapour deposition of lithium manganese oxide thin films via single solid source precursor

Pubblicato online: 06 gen 2016

Pagine: 725 - 731

Ricevuto: 08 dic 2014

Accettato: 25 ago 2015

DOI: https://doi.org/10.1515/msp-2015-0102

Parole chiave
MOCVD, thin film, pyrolysis, LiMnO, Rutherford backscattering, bandgap energy

© 2015 K.O. Oyedotun et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Metal-organic chemical vapour deposition of lithium manganese oxide thin films via single solid source precursor

Pubblicato online: 06 gen 2016

Pagine: 725 - 731

Ricevuto: 08 dic 2014

Accettato: 25 ago 2015

DOI: https://doi.org/10.1515/msp-2015-0102

Parole chiaveMOCVD, thin film, pyrolysis, LiMnO, Rutherford backscattering, bandgap energy

© 2015 K.O. Oyedotun et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
MOCVD, thin film, pyrolysis, LiMnO, Rutherford backscattering, bandgap energy