<abstract xmlns="http://www.w3.org/1999/xhtml">Copper sulfide-selenide (CuS0.2Se0.8) thin films were deposited on FTO coated glass substrate (fluorine doped tin oxide) and stainless steel substrates using electrodeposition technique. Deposited thin films were characterized using different characterization techniques viz. X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-Vis spectroscopy, photoluminescence spectroscopy and surface wettability. XRD study showed polycrystalline nature with cubic phase of the films. Scanning electron microscopy showed that the surface area of the substrate was covered by the nanoplatelets structure of a thickness of 140 to 150 nm and optical study showed that the direct band gap was ~1.90 eV. Surface wettability showed hydrophobic nature of the CuS0.2Se0.8 thin films. </abstract>

Copper sulfide-selenide (CuS0.2Se0.8) thin films were deposited on FTO coated glass substrate (fluorine doped tin oxide) and stainless steel substrates using electrodeposition technique. Deposited thin films were characterized using different characterization techniques viz. X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-Vis spectroscopy, photoluminescence spectroscopy and surface wettability. XRD study showed polycrystalline nature with cubic phase of the films. Scanning electron microscopy showed that the surface area of the substrate was covered by the nanoplatelets structure of a thickness of 140 to 150 nm and optical study showed that the direct band gap was ~1.90 eV. Surface wettability showed hydrophobic nature of the CuS0.2Se0.8 thin films.

Electrochemical synthesis of nanoplatelets-like CuS0.2Se0.8 thin film for photoluminescence applications

Thin film, Earth and Space Science Laboratory, Department of Physics, Shivaji University, Kolhapur, India

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Electrochemical synthesis of nanoplatelets-like CuSSe thin film for photoluminescence applications

Copper sulfide-selenide (CuS0.2Se0.8) thin films were deposited on FTO coated glass substrate (fluorine doped tin oxide) and stainless steel substrates using...

Electrochemical synthesis of nanoplatelets-like CuS_0.2Se_0.8 thin film for photoluminescence applications

Pubblicato online: 11 lug 2015

Pagine: 397 - 401

Ricevuto: 04 nov 2014

Accettato: 03 feb 2015

DOI: https://doi.org/10.1515/msp-2015-0055

© 2015

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.