<abstract xmlns="http://www.w3.org/1999/xhtml">TiO2 has an easily tunable bandgap and a great absorption dye ability being widely used in many fields and in a number of fascinating applications. In this study, a wet chemical route, particularly a sol gel method using spin-coating is adopted to deposit TiO2 thin films onto soda lime glass and silicon substrates. TiO2 films were prepared by using an alcoholic solution of analytical reagent grade TiCl4 as titanium precursor at various experimental conditions. The accent was put on the conditions of preparation (spin time, spin speed, precursor concentration, number of coating layers <italic>etc</italic>), doping and on the post-deposit treatment namely the drying and the crystallization. The results showed a strong dependence on the drying temperature and on the temperature and duration of the crystallization. We found that the solution preparation and its color are important for getting a reproducible final product. The Raman spectra recorded at room temperature, showed the characteristic peaks of anatase which appear at 143 and around 396 cm−1. These peaks confirm the presence of TiO2.The X-ray diffraction (XRD) was used to identify the crystalline characteristic of TiO2 while the chemical states and relative amounts of the main elements existing in the samples were investigated by X-ray Photoelectron Spectroscopy (XPS). The morphology of the samples was visualized by AFM. We show by this work the feasibility to obtain different nanostructured TiO2 by changing the concentration of the solution. Photocatalytic activity of TiO2 films was evaluated. Rhodamine B is a recalcitrant dye and TiO2 was successfully tested for its oxidation. An abatement of 60% was obtained under sunlight for an initial concentration of 10 mg/l.</abstract>

TiO2 has an easily tunable bandgap and a great absorption dye ability being widely used in many fields and in a number of fascinating applications. In this study, a wet chemical route, particularly a sol gel method using spin-coating is adopted to deposit TiO2 thin films onto soda lime glass and silicon substrates. TiO2 films were prepared by using an alcoholic solution of analytical reagent grade TiCl4 as titanium precursor at various experimental conditions. The accent was put on the conditions of preparation (spin time, spin speed, precursor concentration, number of coating layers etc), doping and on the post-deposit treatment namely the drying and the crystallization. The results showed a strong dependence on the drying temperature and on the temperature and duration of the crystallization. We found that the solution preparation and its color are important for getting a reproducible final product. The Raman spectra recorded at room temperature, showed the characteristic peaks of anatase which appear at 143 and around 396 cm−1. These peaks confirm the presence of TiO2.The X-ray diffraction (XRD) was used to identify the crystalline characteristic of TiO2 while the chemical states and relative amounts of the main elements existing in the samples were investigated by X-ray Photoelectron Spectroscopy (XPS). The morphology of the samples was visualized by AFM. We show by this work the feasibility to obtain different nanostructured TiO2 by changing the concentration of the solution. Photocatalytic activity of TiO2 films was evaluated. Rhodamine B is a recalcitrant dye and TiO2 was successfully tested for its oxidation. An abatement of 60% was obtained under sunlight for an initial concentration of 10 mg/l.

Characterization of TiO2 films obtained by a wet chemical process

Laboratory of Semiconductor Material and Metallic Oxides, Faculty of Physics

University of Sciences and Technology (USTHB)

Centro de Qumica-Física Molecular and IN, Instituto Superior Técnico

Laboratory of Storage and Valorization of Renewable Energies, Faculty of Chemistry

Journal of Electrical Engineering

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Characterization of TiO films obtained by a wet chemical process

TiO2 has an easily tunable bandgap and a great absorption dye ability being widely used in many fields and in a number of fascinating applications. In this...

Characterization of TiO₂ films obtained by a wet chemical process

Pubblicato online: 29 dic 2017

Pagine: 31 - 36

Ricevuto: 23 apr 2017

DOI: https://doi.org/10.1515/jee-2017-0052

Parole chiave
Titanium oxide, spin-coating, XPS, Raman, XRD

© 2017 Asma Sedik et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Characterization of TiO2 films obtained by a wet chemical process

Pubblicato online: 29 dic 2017

Pagine: 31 - 36

Ricevuto: 23 apr 2017

DOI: https://doi.org/10.1515/jee-2017-0052

Parole chiaveTitanium oxide, spin-coating, XPS, Raman, XRD

© 2017 Asma Sedik et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Characterization of TiO₂ films obtained by a wet chemical process

Parole chiave
Titanium oxide, spin-coating, XPS, Raman, XRD