<abstract xmlns="http://www.w3.org/1999/xhtml"><p>In this work two austenitic stainless steels, REX734 and 316LV were tested in terms of their microstructure and corrosion properties. The REX734 is a newer generation stainless steel, with modified chemical composition, in comparison to the 316LV grade. Potentiodynamic study of corrosion resistance was conducted in physiological saline solution (0.9% NaCl solution). In spite of the similarities of microstructure, grain size and phase structure in both materials, the corrosion tests revealed that the REX734, with lower nickel and higher nitrogen content, had better corrosion resistance than 316LV. Repassivation potential in the REX734 was almost six times higher than for the 316LV steel. Superior corrosion resistance of the REX734 steel was also confirmed by surface observations of both materials, since bigger and more densely distributed pits were detected in 316LV alloy.</p></abstract>

In this work two austenitic stainless steels, REX734 and 316LV were tested in terms of their microstructure and corrosion properties. The REX734 is a newer generation stainless steel, with modified chemical composition, in comparison to the 316LV grade. Potentiodynamic study of corrosion resistance was conducted in physiological saline solution (0.9% NaCl solution). In spite of the similarities of microstructure, grain size and phase structure in both materials, the corrosion tests revealed that the REX734, with lower nickel and higher nitrogen content, had better corrosion resistance than 316LV. Repassivation potential in the REX734 was almost six times higher than for the 316LV steel. Superior corrosion resistance of the REX734 steel was also confirmed by surface observations of both materials, since bigger and more densely distributed pits were detected in 316LV alloy.

Comparison of Corrosion Resistance in Physiological Saline Solution of Two Austenitic Stainless Steels – 316LV and REX734

Acta Mechanica et Automatica

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

In this work two austenitic stainless steels, REX734 and 316LV were tested in terms of their microstructure and corrosion properties. The REX734 is a newer...

Comparison of Corrosion Resistance in Physiological Saline Solution of Two Austenitic Stainless Steels – 316LV and REX734

Pubblicato online: 15 giu 2017

Pagine: 91 - 95

Ricevuto: 31 mar 2016

Accettato: 17 mar 2017

DOI: https://doi.org/10.1515/ama-2017-0014

Parole chiave
REX734 Austenitic Stainless Steel, 316LV Austenitic Stainless Steel, Potentiodynamic Corrosion Tests, XRD Analysis, SEM Observation

© 2017 Bialystok University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Comparison of Corrosion Resistance in Physiological Saline Solution of Two Austenitic Stainless Steels – 316LV and REX734

Pubblicato online: 15 giu 2017

Pagine: 91 - 95

Ricevuto: 31 mar 2016

Accettato: 17 mar 2017

DOI: https://doi.org/10.1515/ama-2017-0014

Parole chiaveREX734 Austenitic Stainless Steel, 316LV Austenitic Stainless Steel, Potentiodynamic Corrosion Tests, XRD Analysis, SEM Observation

© 2017 Bialystok University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
REX734 Austenitic Stainless Steel, 316LV Austenitic Stainless Steel, Potentiodynamic Corrosion Tests, XRD Analysis, SEM Observation