<abstract xmlns="http://www.w3.org/1999/xhtml"><p>Novel polythioamide (PTA) was prepared and blended with polyamide 1010 (PA1010). Based on morphology, molecular weight, polydispersity index, thermal, and shear stress behavior, PA1010/PTA (90:10) blend was opted as matrix for graphene nanoplatelet (GNP) reinforcement. Inclusion of functional GNP resulted in crumpled gyroid morphology. T<sub>0</sub> (502°C) of PA1010/PTA/GNP was increased by 145°C than unfilled blend (357°C). Limiting oxygen index measurement indicated better non-flammability of PA1010/PTA/GNP1-3 nanocomposites (53-55%) relative to PA1010/PTA1-3 (41-48%). PA1010/PTA/GNP1-3 also attained V-0 rating in UL94. Furthermore, PA1010/PTA/GNP3 nanocomposite revealed optimum tensile strength (40 MPa), impact strength (1.9 MPa), and flexural modulus (1373 MPa) to manufacture automotive part.</p></abstract>

Novel polythioamide (PTA) was prepared and blended with polyamide 1010 (PA1010). Based on morphology, molecular weight, polydispersity index, thermal, and shear stress behavior, PA1010/PTA (90:10) blend was opted as matrix for graphene nanoplatelet (GNP) reinforcement. Inclusion of functional GNP resulted in crumpled gyroid morphology. T0 (502°C) of PA1010/PTA/GNP was increased by 145°C than unfilled blend (357°C). Limiting oxygen index measurement indicated better non-flammability of PA1010/PTA/GNP1-3 nanocomposites (53-55%) relative to PA1010/PTA1-3 (41-48%). PA1010/PTA/GNP1-3 also attained V-0 rating in UL94. Furthermore, PA1010/PTA/GNP3 nanocomposite revealed optimum tensile strength (40 MPa), impact strength (1.9 MPa), and flexural modulus (1373 MPa) to manufacture automotive part.

Polyamide 1010/Polythioamide Blend Reinforced with Graphene Nanoplatelet for Automotive Part Application

Nanoscience and Technology Department, National Centre For Physics

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Novel polythioamide (PTA) was prepared and blended with polyamide 1010 (PA1010). Based on morphology, molecular weight, polydispersity index, thermal, and...

Polyamide 1010/Polythioamide Blend Reinforced with Graphene Nanoplatelet for Automotive Part Application

Pubblicato online: 25 ott 2017

Pagine: 24 - 36

DOI: https://doi.org/10.1515/adms-2017-0013

Parole chiave
Polyamide 1010, graphene nanoplatelet, automotive

© 2017 A. Kausar, published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Polyamide 1010/Polythioamide Blend Reinforced with Graphene Nanoplatelet for Automotive Part Application

Pubblicato online: 25 ott 2017

Pagine: 24 - 36

DOI: https://doi.org/10.1515/adms-2017-0013

Parole chiavePolyamide 1010, graphene nanoplatelet, automotive

© 2017 A. Kausar, published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
Polyamide 1010, graphene nanoplatelet, automotive