<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>Porous carbons loaded with magnesium oxide were prepared through one-step process. Poly(ethylene terephthalate) and natural magnesite were used as carbon source and MgO precursor, respectively. An impact of a temperature and relative amounts of raw components used for preparations on the textural parameters of resulting hybrid materials is presented and discussed. As found, pore structure parameters tend to decrease along with MgO loading and temperature used during preparation process. Micropore area is the parameter being reduced primarily.</p></abstract>

Porous carbons loaded with magnesium oxide were prepared through one-step process. Poly(ethylene terephthalate) and natural magnesite were used as carbon source and MgO precursor, respectively. An impact of a temperature and relative amounts of raw components used for preparations on the textural parameters of resulting hybrid materials is presented and discussed. As found, pore structure parameters tend to decrease along with MgO loading and temperature used during preparation process. Micropore area is the parameter being reduced primarily.

Preparation and properties of porous carbon material containing magnesium oxide

Institute of Chemical and Environmental Engineering, West Pomeranian University of Technology in Szczecin, ul. Pułaskiego 10, 70-322 Szczecin, Poland

Instituto de Bioingeniería, Universidad Miguel Hernández, Edificio Vinalopo, Avda. de la Universidad s/n, 03202-Elche, Alicante, Spain

Polish Journal of Chemical Technology

{"article-title":"Preparation and properties of porous carbon material containing magnesium oxide"}

Porous carbons loaded with magnesium oxide were prepared through one-step process. Poly(ethylene terephthalate) and natural magnesite were used as carbon...

Preparation and properties of porous carbon material containing magnesium oxide

Publié en ligne: 02 janv. 2012

Pages: 42 - 46

DOI: https://doi.org/10.2478/v10026-011-0047-0

Mots clés
porous carbon, MgO, porosity

This content is open access.

Preparation and properties of porous carbon material containing magnesium oxide

Publié en ligne: 02 janv. 2012

Pages: 42 - 46

DOI: https://doi.org/10.2478/v10026-011-0047-0

Mots clésporous carbon, MgO, porosity

This content is open access.

Mots clés
porous carbon, MgO, porosity