Designation | Width [mm] | Thickness [mm] | Length [mm] |
---|---|---|---|
1C | 25 | 2 | 250 |
2C | 25 | 2 | 250 |
3C | 25 | 2 | 250 |
4C | 25 | 2 | 250 |
5C | 25 | 2 | 250 |
6C | 25 | 2 | 250 |
7C | 25 | 2 | 250 |
8C | 25 | 2 | 250 |
9C | 25 | 2 | 250 |
Designation | Width [mm] | Thickness [mm] | Length [mm] |
---|---|---|---|
1D | 26 | 2 | 250 |
2D | 26 | 2 | 250 |
3D | 26 | 2 | 250 |
4D | 26 | 2 | 250 |
5D | 26 | 2 | 250 |
6D | 26 | 2 | 250 |
7D | 26 | 2 | 250 |
8D | 26 | 2 | 250 |
9D | 26 | 2 | 250 |
Parameter | Biaxial fabric IMS65 CTLX | Symmetric Interglass 02037 | Modular fabric IMS65 |
---|---|---|---|
Density of fabric sheet g/m2] | 6,8 | 47,5 | 27,2 |
thickness [mm] | 0,19 | 0,21 | 0,21 |
tensile strength [MPa] | 513 | 443 | 1450 |
Designation | Width [mm] | Thickness [mm] | Length [mm] |
---|---|---|---|
1E | 26 | 2 | 250 |
2E | 26 | 2 | 250 |
3E | 26 | 2 | 248 |
4E | 26 | 2 | 250 |
5E | 26 | 2 | 250 |
6E | 26 | 2 | 250 |
7E | 26 | 2 | 250 |
8E | 26 | 2 | 250 |
Designation | Section area S0 [mm2] | Maximum tensile force Fm [kN] | Tensile strength limit Rm [MPa] |
---|---|---|---|
D1 | 50 | 16.950 | 339.009 |
D2 | 50 | 40.040 | 800.795 |
D3 | 50 | 36.356 | 727.115 |
D4 | 50 | 26.894 | 537.885 |
D5 | 50 | 33.539 | 670.782 |
D6 | 50 | 14.555 | 291.109 |
Designation | Section area S0 [mm2] | Maximum tensile force Fm [kN] | Tensile strength limit Rm [MPa] |
---|---|---|---|
E1 | 50 | 18.425 | 368.501 |
E2 | 50 | 21.414 | 428.278 |
E4 | 50 | 9.995 | 199.897 |
E5 | 50 | 13.102 | 262.031 |
Parameter | D-series | E-series |
---|---|---|
Maximum tensile force Fm [kN] | 28.056 | 15.734 |
tensile strength limit Rm [MPa] | 561.116 | 314.677 |
Lp. | Time t [s] | Force F [kN] | Tension σ [MPa] | Tensometer 1 | Tensometer 2 | Poisson’s ratio [-] |
---|---|---|---|---|---|---|
1 | 44 | 0.308 | 6.152 | 120.776 | 4.623 | -0.038 |
2 | 44.2 | 0.310 | 6.202 | 121.518 | 4.547 | -0.037 |
3 | 44.4 | 0.312 | 6.242 | 122.241 | 4.585 | -0.038 |
4 | 44.6 | 0.314 | 6.287 | 123.060 | 4.585 | -0.037 |
5 | 44.8 | 0.316 | 6.328 | 123.859 | 4.585 | -0.037 |
6 | 45 | 0.318 | 6.362 | 124.563 | 4.566 | -0.037 |
7 | 45.2 | 0.320 | 6.402 | 125.400 | 4.642 | -0.037 |
8 | 45.4 | 0.322 | 6.449 | 126.275 | 4.642 | -0.037 |
9 | 45.6 | 0.324 | 6.489 | 126.846 | 4.566 | -0.036 |
10 | 45.8 | 0.327 | 6.532 | 127.455 | 4.623 | -0.036 |
11 | 46 | 0.328 | 6.559 | 128.101 | 4.452 | -0.035 |
12 | 46.2 | 0.330 | 6.600 | 129.053 | 4.566 | -0.035 |
13 | 46.4 | 0.332 | 6.639 | 129.757 | 4.623 | -0.036 |
14 | 46.6 | 0.334 | 6.685 | 130.308 | 4.604 | -0.035 |
15 | 46.8 | 0.337 | 6.734 | 130.955 | 4.490 | -0.034 |
16 | 47 | 0.339 | 6.774 | 131.526 | 4.414 | -0.034 |
17 | 47.2 | 0.341 | 6.814 | 132.287 | 4.262 | -0.032 |
18 | 47.4 | 0.343 | 6.858 | 133.200 | 4.224 | -0.032 |
19 | 47.6 | 0.345 | 6.894 | 133.847 | 4.319 | -0.032 |
20 | 47.8 | 0.347 | 6.935 | 134.437 | 4.414 | -0.033 |
21 | 48 | 0.349 | 6.981 | 135.331 | 4.585 | -0.034 |
22 | 48.2 | 0.351 | 7.026 | 136.302 | 4.776 | -0.035 |
23 | 48.4 | 0.354 | 7.076 | 137.234 | 4.699 | -0.034 |
24 | 48.6 | 0.357 | 7.131 | 138.261 | 4.776 | -0.035 |
25 | 48.8 | 0.358 | 7.167 | 139.060 | 4.699 | -0.034 |
26 | 49 | 0.361 | 7.211 | 139.917 | 4.604 | -0.033 |
27 | 49.2 | 0.363 | 7.266 | 140.830 | 4.433 | -0.031 |
28 | 49.4 | 0.366 | 7.312 | 141.705 | 4.528 | -0.032 |
29 | 49.6 | 0.368 | 7.356 | 142.599 | 4.661 | -0.033 |
30 | 49.8 | 0.370 | 7.401 | 143.551 | 4.680 | -0.033 |
Maximum test force FN (tension, compression) | 100 kN |
Test temperature | Room up to 1,200°C |
Number of furnaces | 2 |
Temperature control | Three thermocouples in furnace chamber |
Traverse speed | 0.0005 do 750 mm/min |
Accuracy of set rate | 0.003% Vnom |
Measurement of force in the range from 0.4% to 100% Fnom | Class 1 |
Measurement of force in the range from 2% to 100% Fnom | Class 0.5 |
Initial measurement length of extensometer | 11–50 mm |