<abstract xmlns="http://www.w3.org/1999/xhtml"><p> When a concrete structure is exposed to fire and cooling, some deterioration in its chemical resistivity and mechanical properties takes place. This deterioration can reach a level at which the structure may have to be thoroughly renovated or completely replaced. In this investigation, four types of cement mortars, ground clay bricks (GCB)/sand namely 0/3, 1/2, 2/1 and 3/0, were used. Three different cement contents were used: 350, 400 and 450 kg/m3. All the mortars were prepared and cured in tap water for 3 months and then kept in laboratory atmospheric conditions up to 6 months. The specimens were subjected to elevated temperatures up to 700°C for 3h and then cooled by three different conditions: water, furnace, and air cooling. The results show that all the mortars subjected to fire, irrespective of cooling mode, suffered a significant reduction in compressive strength. However, the mortars cooled in air exhibited a relativity higher reduction in compressive strength rather than those water or furnace cooled. The mortars containing GCB/sand (3/0) and GCB/sand (1/2) exhibited a relatively higher thermal stability than the others.</p></abstract>

When a concrete structure is exposed to fire and cooling, some deterioration in its chemical resistivity and mechanical properties takes place. This deterioration can reach a level at which the structure may have to be thoroughly renovated or completely replaced. In this investigation, four types of cement mortars, ground clay bricks (GCB)/sand namely 0/3, 1/2, 2/1 and 3/0, were used. Three different cement contents were used: 350, 400 and 450 kg/m3. All the mortars were prepared and cured in tap water for 3 months and then kept in laboratory atmospheric conditions up to 6 months. The specimens were subjected to elevated temperatures up to 700°C for 3h and then cooled by three different conditions: water, furnace, and air cooling. The results show that all the mortars subjected to fire, irrespective of cooling mode, suffered a significant reduction in compressive strength. However, the mortars cooled in air exhibited a relativity higher reduction in compressive strength rather than those water or furnace cooled. The mortars containing GCB/sand (3/0) and GCB/sand (1/2) exhibited a relatively higher thermal stability than the others.

Coupled Effect of Elevated Temperature and Cooling Conditions on the Properties of Ground Clay Brick Mortars

Ali ABD EL AZIZ Faculty of Engineering, Fayoum University, Fayoum, Egypt

Chemistry Department, Faculty of Science, Fayoum University, Fayoum, Egypt

Chemistry Department, College of Science, Al-Imam Muhammad Ibn Saud Islamic University (IMSIU), P.O. Box 90950, Riyadh 11623, Saudi Arabia Permanent Address: Chemistry Department, Faculty of Science, Benha University, Benha, Egypt

Slovak Journal of Civil Engineering

When a concrete structure is exposed to fire and cooling, some deterioration in its chemical resistivity and mechanical properties takes place. This...

Coupled Effect of Elevated Temperature and Cooling Conditions on the Properties of Ground Clay Brick Mortars

Publié en ligne: 29 janv. 2014

Pages: 41 - 50

DOI: https://doi.org/10.2478/sjce-2013-0020

Mots clés
Ground clay bricks, fire resistance, XRD, microstructure, compressive strength, and cooling mode

This content is open access.

Coupled Effect of Elevated Temperature and Cooling Conditions on the Properties of Ground Clay Brick Mortars

Publié en ligne: 29 janv. 2014

Pages: 41 - 50

DOI: https://doi.org/10.2478/sjce-2013-0020

Mots clésGround clay bricks, fire resistance, XRD, microstructure, compressive strength, and cooling mode

This content is open access.

Mots clés
Ground clay bricks, fire resistance, XRD, microstructure, compressive strength, and cooling mode