<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>Cavitation erosion studies of steels produced by Electroslag Refining (ESR) and Argon Oxygen Decarburization (AOD refining) have been carried out. The experiments were conducted using the modified ultrasonically induced cavitation test method. Erosion rates were measured and the morphology of damages under cavitation action was studied by scanning electron microscopy and optical microscopy techniques. The present work is aimed at understanding the cavitation erosion behaviour of electroslag refined steel (ESR) compared with the steel produced by Argon Oxygen Decarburization (AOD refining), commonly used in the production of hydraulic machinery parts (Pelton blades). The results exhibited lower cavitation rate of ESR steel compared with AOD steel, as a consequence of its better mechanical properties and homogeneous and fine-grained microstructure.</p></abstract>

Cavitation erosion studies of steels produced by Electroslag Refining (ESR) and Argon Oxygen Decarburization (AOD refining) have been carried out. The experiments were conducted using the modified ultrasonically induced cavitation test method. Erosion rates were measured and the morphology of damages under cavitation action was studied by scanning electron microscopy and optical microscopy techniques. The present work is aimed at understanding the cavitation erosion behaviour of electroslag refined steel (ESR) compared with the steel produced by Argon Oxygen Decarburization (AOD refining), commonly used in the production of hydraulic machinery parts (Pelton blades). The results exhibited lower cavitation rate of ESR steel compared with AOD steel, as a consequence of its better mechanical properties and homogeneous and fine-grained microstructure.

Comparative cavitation erosion test on steels produced by ESR and AOD refining

Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11000, Belgrade, Serbia

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Comparative cavitation erosion test on steels produced by ESR and AOD refining"}

Cavitation erosion studies of steels produced by Electroslag Refining (ESR) and Argon Oxygen Decarburization (AOD refining) have been carried out. The...

Comparative cavitation erosion test on steels produced by ESR and AOD refining

Publié en ligne: 29 févr. 2012

Pages: 216 - 222

DOI: https://doi.org/10.2478/s13536-011-0034-4

Mots clés
cavitation, refining, SEM, optical microscopy, microhardness

© 2011 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Comparative cavitation erosion test on steels produced by ESR and AOD refining

Publié en ligne: 29 févr. 2012

Pages: 216 - 222

DOI: https://doi.org/10.2478/s13536-011-0034-4

Mots cléscavitation, refining, SEM, optical microscopy, microhardness

© 2011 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Mots clés
cavitation, refining, SEM, optical microscopy, microhardness