1 | 70 | 30 | 6 | |
1 | 65 | 35 | 6 | |
1 | 60 | 40 | 6 | |
2 | 70 | 30 | 6 | |
2 | 65 | 35 | 6 | |
2 | 60 | 40 | 6 | |
- | 00 | 100 | 8 |
Bentonite | 17.2 | 84.454 | 278.142 |
Glass Waste 1 | 0.536 | 3.919 | 142.64 |
Glass Waste 2 | 5.735 | 53.713 | 168.7 |
Humidity (%) | 6.83582 | 6.89445 | 6.57 | 11.7428 |
Shrinking (%) | 3.916 | −7.182 | −5.8492 | −4.78 |
Mass loss (%) | 15.417 | 4.475 | 4.78 | 8.4946 |
Density (g/cm3) | 1.542 | 2.078 | 2.02 | 2.04 |
Mass specific (g/cm3) | 2.33278 | 2.2003 | 2.3371 | 2.34 |
Absorption (%) | 22.182 | 2.6598 | 6.57 | 6.18 |
Porosity (%) | 33.904 | 5.525 | 13.3 | 12.62 |
Resistance flexion (MPa) | 19.2444 | 32.6762 | 24.6616 | 14.2101 |
Breaking strength (N) | 714 | 729 | 1062 | 500 |
Hardness (HV) | 90 | 188 | 153 | 208 |
Humidity (%) | 6.1809 | 5.79 | 7.4779 | 11.7428 |
Shrinking (%) | −7.08 | −6.097 | −5.335 | −4.78 |
Mass loss (%) | 4.3195 | 4.64 | 5.042 | 8.4946 |
Density (g/cm3) | 2.1325 | 2.09 | 2.065 | 2.04 |
Mass specific (g/cm3) | 2.1605 | 2.29 | 2.36 | 2.34 |
Absorption (%) | 6.5625 | 4.29 | 6.07 | 6.18 |
Porosity (%) | 13.975 | 8.9625 | 12.53 | 12.62 |
Resistance flexion (MPa) | 29.9578 | 28.844 | 31.734 | 14.2101 |
Breaking strength (N) | 553 | 742 | 743 | 500 |
Hardness (HV) | 159 | 186 | 167 | 208 |
Bentonite | 14.16 | 55.94 | 3.14 | 13.57 | 5.91 | 1.74 | 0.41 | 2.19 | 2.47 | 0.15 | 0.33 |
Glass waste | 2.67 | 70.26 | 0.99 | 0.44 | 11.79 | 1.68 | 0.21 | 0.52 | 11.43 | 0.01 | 0.02 |