Sulfonation Modification of Guar Gum and Its Performance as a Fracturing Fluids Thickener

To solve the contradiction between reducing water-insoluble content and maintaining high viscosity in the preparation of modified guar gum for oilfield fracturing fluid, in this work, sodium 3-chloro-2-hydroxypropylsulfonate was used as a modifier to prepare sulfonated guar gum. Orthogonal and single-factor extrapolation experiments were conducted to explore the effects of reaction conditions and the optimal process was determined as follows: reaction temperature of 26 ^oC, reaction time of 2.0 h, sodium hydroxide as a mass fraction of guar gum of 1.0%, and sodium 3-chloro-2-hydroxypropyl sulfonate dosage as a mass fraction of guar gum of 0.5%. Furtherly, the temperature stability, filtration property, and inhibition of formation clay of the sulfonated products were investigated. The results showed that the apparent viscosity of 0.6% solution of guar gum was increased by 33%, the water-insoluble content was decreased by 0.42%, and the temperature stability, filtration resistance, and clay inhibition were all improved. Especially, the viscosity of cross-linked sulfonated guar gum is 100% higher than that of unmodified guar gum. The structure of sulfonated guar gum was characterized and confirmed by infrared spectrum, DSC, thermogravimetric, and elemental analysis.