Connexion
S'inscrire
Réinitialiser le mot de passe
Publier & Distribuer
Solutions d'édition
Solutions de distribution
Thèmes
Architecture et design
Arts
Business et économie
Chimie
Chimie industrielle
Droit
Géosciences
Histoire
Informatique
Ingénierie
Intérêt général
Linguistique et sémiotique
Littérature
Mathématiques
Musique
Médecine
Pharmacie
Philosophie
Physique
Sciences bibliothécaires et de l'information, études du livre
Sciences des matériaux
Sciences du vivant
Sciences sociales
Sport et loisirs
Théologie et religion
Études classiques et du Proche-Orient ancient
Études culturelles
Études juives
Publications
Journaux
Livres
Comptes-rendus
Éditeurs
Blog
Contact
Chercher
EUR
USD
GBP
Français
English
Deutsch
Polski
Español
Français
Italiano
Panier
Home
Journaux
Materials Science-Poland
Édition 40 (2022): Edition 4 (December 2022)
Accès libre
A new approach to flux deposition for brazing aluminium by low pressure cold spraying
Tomasz Wojdat
Tomasz Wojdat
,
Marcin Winnicki
Marcin Winnicki
et
Jaroslaw Pabian
Jaroslaw Pabian
| 20 avr. 2023
Materials Science-Poland
Édition 40 (2022): Edition 4 (December 2022)
À propos de cet article
Article précédent
Article suivant
Résumé
Article
Figures et tableaux
Références
Auteurs
Articles dans cette édition
Aperçu
PDF
Citez
Partagez
Publié en ligne:
20 avr. 2023
Pages:
114 - 124
Reçu:
10 janv. 2023
Accepté:
08 mars 2023
DOI:
https://doi.org/10.2478/msp-2022-0048
Mots clés
flux deposition
,
low-pressure cold spraying
,
aluminium alloy
,
brazing
,
flux powder
,
brazed joints
,
B-AlSi12 filler metal
© 2022 Tomasz Wojdat et al., published by Sciendo
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Fig. 1
An exemplary roughness profile for the PFR 2 sample (DM). DM, digital microscope
Fig. 2
Micrographs (SEM, BSE) of flux coatings: (A) PFR 1 and (B) PFR 2. 1 – substrate (AA3003), 2 – flux (Nocolok) coating. SEM, scanning electron microscope
Fig. 3
Micrograph (SEM, BSE) of the PFR 3 coating. 1 – substrate (AA3003), 2 – flux (Nocolok) coating. SEM, scanning electron microscope
Fig. 4
(A) EDS analysis of the PFR 3 coating's surface and (B) elements distribution of aluminium, (C) fluorine and (D) potassium. Table – chemical composition of the coating depended on powder feed rate determined based on the surface EDS analysis. EDS, energy dispersive spectrometry
Fig. 5
Results of the B-AlSi12 filler metal spreadability on AA3003 substrates
Fig. 6
Results of the B-AlSi12 filler metal wettability test on AA3003 substrates
Fig. 7
Cross-section (DM) of brazed joints for various samples: (A) PFR 1, (B) PFR 2 and (C) PFR 3. DM, digital microscope
Fig. 8
Microstructure (SEM, BSE) of brazed joints (A) PFR 1, (B) PFR 2, (C) PFR 3 and phase precipitates of Si in the microstructure of (A) PFR1, (B) PFR 2 and (C) PFR 3 samples. 1 – solid solution dendrites α-Al, 2 – eutectic (α + Si), 3 – irregularly shaped intermetallic phase and 4 – coniferous Si phase precipitates. SEM, scanning electron microscope
Fig. 9
EDS of the PFR 1 sample presenting the (A) analysed region and (B) distribution of the elements: Si, (C) Fe, and (D) Mn (mag. 2,000×, 20 keV). EDS, elemental mapping
Fig. 10
SEM micrograph (BSE) of the PFR 1 sample with EDS analysis (magnification 2,000×, 20 keV). EDS, energy dispersive spectrometry; SEM, scanning electron microscope
LPCS process parameters during flux deposition
Powder feed rate, g/min
Traverse speed, mm/s
Gas preheating temperature, °C
Gas pressure, MPa
Standoff, mm
Number of spray passes
4.5
20
200
05
10
1
6.3
8.5
Results of roughness and thickness measurements
Parameter
Samples
PFR 1
PFR 2
PFR 3
Mean roughness
Ra
(μm)
16.1
24.3
35.7
Mean thickness
t
(μm)
5.3
16.2
83.5