<abstract xmlns="http://www.w3.org/1999/xhtml"><p>In this paper, results of investigation on the impact of firing temperature on insulating properties of Low Temperature Cofired Ceramics are presented. Dissipation factor, volume resistivity and breakdown electric field intensity were determined for firing peak temperature in the range from 800 °C to 900 °C. The tests were performed for two commercial LTCC materials: 951 Green Tape (DuPont, USA) and SK47 (Keko, Slovenia). The results showed that the firing temperature had a significant effect on the dielectric loss factor, volume resistivity and lifetime at applied high voltage. No clear tendency was observed for dielectric strength in the analyzed firing temperature range.</p></abstract>

In this paper, results of investigation on the impact of firing temperature on insulating properties of Low Temperature Cofired Ceramics are presented. Dissipation factor, volume resistivity and breakdown electric field intensity were determined for firing peak temperature in the range from 800 °C to 900 °C. The tests were performed for two commercial LTCC materials: 951 Green Tape (DuPont, USA) and SK47 (Keko, Slovenia). The results showed that the firing temperature had a significant effect on the dielectric loss factor, volume resistivity and lifetime at applied high voltage. No clear tendency was observed for dielectric strength in the analyzed firing temperature range.

Impact of firing temperature on insulating properties of Low Temperature Co-fired Ceramics

Wroclaw University of Science and Technology

Faculty of Microsystem Electronics and Photonics

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

In this paper, results of investigation on the impact of firing temperature on insulating properties of Low Temperature Cofired Ceramics are presented....

Impact of firing temperature on insulating properties of Low Temperature Co-fired Ceramics

Publié en ligne: 08 mai 2020

Pages: 189 - 196

Reçu: 08 janv. 2019

Accepté: 15 juil. 2019

DOI: https://doi.org/10.2478/msp-2020-0012

Mots clés
LTCC, ceramics, breakdown, volume resistivity, high voltage

© 2020 Arkadiusz P. Dabrowski, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Impact of firing temperature on insulating properties of Low Temperature Co-fired Ceramics

Publié en ligne: 08 mai 2020

Pages: 189 - 196

Reçu: 08 janv. 2019

Accepté: 15 juil. 2019

DOI: https://doi.org/10.2478/msp-2020-0012

Mots clésLTCC, ceramics, breakdown, volume resistivity, high voltage

© 2020 Arkadiusz P. Dabrowski, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Mots clés
LTCC, ceramics, breakdown, volume resistivity, high voltage