Reliability of Non - Destructive Technologies in Corrosion Detection of Reinforced Concrete Structures

In this paper, the reliability of two nondestructive corrosion detection methods, Half-Cell Potential (HCP) and Electrical Resistivity (ER), was evaluated, considering the Weight Loss (WL) as the reference method. The specimens prepared for this work were placed in Al-Nasiriya Power Station where subjected to three different exposure conditions. They were high relative humidity, high temperature T and laboratory setting R. The concrete mixes included four chloride contents, 0 %, 1.5 %, 3 % and 4 % by weight of cement to generate multiple corrosion degrees. The results showed that exposure to high temperatures has slightly increased the corrosion activity of the T specimens. While the exposure to high relative humidity has clearly increased the corrosion probability of the RH specimens, comparing with the reference R specimens. However, for such environmental conditions, it was found that the reliabilities of the HCP and the ER techniques still questionable and need further investigation.