<p>Thin films of cobalt sulfide were grown on glass substrates at four different temperatures (250 °C, 300 °C, 350 °C and 400 °C) using spray-pyrolysis technique. The precursor solutions were prepared using cobalt chloride and thiourea. The effect of deposition temperature on the structural, morphological, and optical properties of cobalt sulfide thin films was investigated using different experimental techniques such as X-ray diffraction (XRD), and UV-visible spectrophotometry, Fourier Transform Infrared Spectroscopy (FT-IR) and four-probe method. The XRD analysis showed that crystallite size varies from 9.76 to 14.11 nm with increasing the deposition temperature. UV-visible data analysis shows a decrease in the band gap energies with increasing temperature (1.82 eV for 250 °C, 1.76 eV for 300 °C, 1.72 eV for 350 °C, and 1.65 eV for 400 °C). The analysis of the chemical composition by FTIR confirmed the presence of Co, S elements. On the other hand, the electrical conductivity of the cobalt sulfide thin films increased owing to the increase in the crystallite size and reduction of defects density.</p>
</abstract>

Thin films of cobalt sulfide were grown on glass substrates at four different temperatures (250 °C, 300 °C, 350 °C and 400 °C) using spray-pyrolysis technique. The precursor solutions were prepared using cobalt chloride and thiourea. The effect of deposition temperature on the structural, morphological, and optical properties of cobalt sulfide thin films was investigated using different experimental techniques such as X-ray diffraction (XRD), and UV-visible spectrophotometry, Fourier Transform Infrared Spectroscopy (FT-IR) and four-probe method. The XRD analysis showed that crystallite size varies from 9.76 to 14.11 nm with increasing the deposition temperature. UV-visible data analysis shows a decrease in the band gap energies with increasing temperature (1.82 eV for 250 °C, 1.76 eV for 300 °C, 1.72 eV for 350 °C, and 1.65 eV for 400 °C). The analysis of the chemical composition by FTIR confirmed the presence of Co, S elements. On the other hand, the electrical conductivity of the cobalt sulfide thin films increased owing to the increase in the crystallite size and reduction of defects density.

Substrate Temperature Effect on the Structural, Optical and Morphological Proprties of Cobalt Sulfide Thin Films Deposited Using Spray Pyrolisis

Department of Biology, Faculty of Sciences

Department of Physics, Faculty of Matter Sciences

Annals of West University of Timisoara - Physics

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Thin films of cobalt sulfide were grown on glass substrates at four different temperatures (250 °C, 300 °C, 350 °C and 400 °C) using spray-pyrolysis technique....

Substrate Temperature Effect on the Structural, Optical and Morphological Proprties of Cobalt Sulfide Thin Films Deposited Using Spray Pyrolisis

Publié en ligne: 29 mai 2024

Pages: -

Reçu: 29 janv. 2024

Accepté: 14 mai 2024

DOI: https://doi.org/10.2478/awutp-2024-0010

Mots clés
Cobalt sulfide, Spray-pyrolysis, FTIR, Optical gap, Conductivity

© 2024 Abdelouahab Gahtar et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Substrate Temperature Effect on the Structural, Optical and Morphological Proprties of Cobalt Sulfide Thin Films Deposited Using Spray Pyrolisis

Publié en ligne: 29 mai 2024

Pages: -

Reçu: 29 janv. 2024

Accepté: 14 mai 2024

DOI: https://doi.org/10.2478/awutp-2024-0010

Mots clésCobalt sulfide, Spray-pyrolysis, FTIR, Optical gap, Conductivity

© 2024 Abdelouahab Gahtar et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Mots clés
Cobalt sulfide, Spray-pyrolysis, FTIR, Optical gap, Conductivity