Semiconductive nanometer-size material ZnCo2O4 was synthesized by a solution combustion reaction of inorganic reagents of Zn(NO3)3. 6H2O, Co(NO3)3.6H2O and glycine as a fuel. The process was a convenient, environment friendly, inexpensive and efficient preparation method for the ZnCo2O4 nanomaterial. The synthesized materials were characterized by TG/DTA, XRD, EDX, SEM, and TEM. Conductance responses of the nanocrystalline ZnCo2O4 thick film were measured by exposing the film to reducing gases like Acetone, Ethanol and CO2. It was found that the sensors exhibited various sensing responses to these gases at different operating temperature. Furthermore, the sensor exhibited a fast response and a good recovery. The results demonstrated that ZnCo2O4 can be used as a new type of gas-sensing material which has a high sensitivity and good selectivity to Ethanol 200 ppm.
</abstract>

Semiconductive nanometer-size material ZnCo2O4 was synthesized by a solution combustion reaction of inorganic reagents of Zn(NO3)3. 6H2O, Co(NO3)3.6H2O and glycine as a fuel. The process was a convenient, environment friendly, inexpensive and efficient preparation method for the ZnCo2O4 nanomaterial. The synthesized materials were characterized by TG/DTA, XRD, EDX, SEM, and TEM. Conductance responses of the nanocrystalline ZnCo2O4 thick film were measured by exposing the film to reducing gases like Acetone, Ethanol and CO2. It was found that the sensors exhibited various sensing responses to these gases at different operating temperature. Furthermore, the sensor exhibited a fast response and a good recovery. The results demonstrated that ZnCo2O4 can be used as a new type of gas-sensing material which has a high sensitivity and good selectivity to Ethanol 200 ppm.

Nanostructured Znco2o4Thick Film As An Ethanol Sensor

International Journal on Smart Sensing and Intelligent Systems

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Nanostructured ZncooThick Film As An Ethanol Sensor

Semiconductive nanometer-size material ZnCo2O4 was synthesized by a solution combustion reaction of inorganic reagents of Zn(NO3)3. 6H2O, Co(NO3)3.6H2O and...

Nanostructured Znco₂o₄Thick Film As An Ethanol Sensor

Publié en ligne: 01 mars 2014

Pages: 178 - 195

Reçu: 22 nov. 2013

Accepté: 10 févr. 2014

DOI: https://doi.org/10.21307/ijssis-2017-651

© 2014 S. V. Bangale et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.