<p>This paper describes the semi-quantitative analysis of metal nanoparticle ink using laser-induced breakdown spectroscopy (LIBS). LIBS can be used to obtain information about the density and chemical composition of silver particles or copper particles, even ultrafine particles. Metal particles have been attracting much attention because of their increased use in new micro-nano technologies. In this work, LIBS was used as a fine metal particle measurement system for nanometallic materials used in printing. Good spectral peak resolutions were obtained when the Ag spectra were recorded at wavelengths of 328.068 nm and 338.289 nm and Cu spectra at 324.754 nm and 327.396 nm.</p>
</abstract>

This paper describes the semi-quantitative analysis of metal nanoparticle ink using laser-induced breakdown spectroscopy (LIBS). LIBS can be used to obtain information about the density and chemical composition of silver particles or copper particles, even ultrafine particles. Metal particles have been attracting much attention because of their increased use in new micro-nano technologies. In this work, LIBS was used as a fine metal particle measurement system for nanometallic materials used in printing. Good spectral peak resolutions were obtained when the Ag spectra were recorded at wavelengths of 328.068 nm and 338.289 nm and Cu spectra at 324.754 nm and 327.396 nm.

Development of Semi-Quantitative Analytical System for Metal Nanoparticle Ink Using Laser-Induced Breakdown Spectroscopy

International Journal on Smart Sensing and Intelligent Systems

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

This paper describes the semi-quantitative analysis of metal nanoparticle ink using laser-induced breakdown spectroscopy (LIBS). LIBS can be used to obtain...

Development of Semi-Quantitative Analytical System for Metal Nanoparticle Ink Using Laser-Induced Breakdown Spectroscopy

Publié en ligne: 01 mars 2012

Pages: 215 - 232

Reçu: 03 févr. 2012

Accepté: 23 févr. 2012

DOI: https://doi.org/10.21307/ijssis-2017-478

© 2012 S. Ikezawa et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.