<abstract xmlns="http://www.w3.org/1999/xhtml">PbZr0:5Ti0:5O3 nanopowders (~27 nm) have been prepared by a controlled reconstructive thermal decomposition and crystallization from an amorphous polymeric precursor with polyvinyl alcohol (PVA) and sucrose at 400 to 700 °C in air. The Rietveld refinement of the XRD profiles which were recorded at room temperature for the PbZr0:5Ti0:5O3 powder prepared by a thermal treatment at 700 °C for 2 h, confirmed the P4mm tetragonal crystal structure of the as prepared PbZr0:5Ti0:5O3 nanopowders, with a = 0.4036 nm and c = 0.4147 nm. A hexagonal symmetry (R3c), with a = 0.5774 nm and c = 1.4212 nm, was also detected from Rietveld refinement analysis. Thus, tetragonal and hexagonal phases were found to coexist with the as prepared PbZr0:5Ti0:5O3 nanopowders. The average particle size (D) of the PbZr0:5Ti0:5O3 powders, estimated with the help of the specific surface area, measured by BET method, was 26.1 nm. Average D value, calculated by D2θ1/2 in the XRD peaks with the Debye-Scherrer relation was ~24 nm. TEM study made it possible to measure the particle size of PbZr0:5Ti0:5O3 powders with an average diameter of 27 nm.</abstract>

PbZr0:5Ti0:5O3 nanopowders (~27 nm) have been prepared by a controlled reconstructive thermal decomposition and crystallization from an amorphous polymeric precursor with polyvinyl alcohol (PVA) and sucrose at 400 to 700 °C in air. The Rietveld refinement of the XRD profiles which were recorded at room temperature for the PbZr0:5Ti0:5O3 powder prepared by a thermal treatment at 700 °C for 2 h, confirmed the P4mm tetragonal crystal structure of the as prepared PbZr0:5Ti0:5O3 nanopowders, with a = 0.4036 nm and c = 0.4147 nm. A hexagonal symmetry (R3c), with a = 0.5774 nm and c = 1.4212 nm, was also detected from Rietveld refinement analysis. Thus, tetragonal and hexagonal phases were found to coexist with the as prepared PbZr0:5Ti0:5O3 nanopowders. The average particle size (D) of the PbZr0:5Ti0:5O3 powders, estimated with the help of the specific surface area, measured by BET method, was 26.1 nm. Average D value, calculated by D2θ1/2 in the XRD peaks with the Debye-Scherrer relation was ~24 nm. TEM study made it possible to measure the particle size of PbZr0:5Ti0:5O3 powders with an average diameter of 27 nm.

Rietveld refinement on XRD and TEM study of nanocrystalline PbZr0:5Ti0:5O3 ceramics prepared with a soft chemistry route

Faculty of Science and Technology, The ICFAI University, Rajawala Road, Central Hope Town, Selaqui, Dehradun-248197, Uttarakhand, India

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Rietveld refinement on XRD and TEM study of nanocrystalline PbZrTiO ceramics prepared with a soft chemistry route

PbZr0:5Ti0:5O3 nanopowders (~27 nm) have been prepared by a controlled reconstructive thermal decomposition and crystallization from an amorphous polymeric...

Rietveld refinement on XRD and TEM study of nanocrystalline PbZr_0:5Ti_0:5O₃ ceramics prepared with a soft chemistry route

Publié en ligne: 13 mars 2015

Pages: 18 - 24

Reçu: 10 sept. 2013

Accepté: 16 janv. 2015

DOI: https://doi.org/10.1515/msp-2015-0040