<abstract xmlns="http://www.w3.org/1999/xhtml">Bilayer antireflective coatings consisting of aluminium oxide Al2O3/MgF2 and Al2O3/SiO2 are presented in this paper. Oxide films were deposited by means of e-gun evaporation in vacuum of 5 × 10-3 Pa in the presence of oxygen, and magnesium fluoride was prepared by thermal evaporation on heated optical lenses made from quartz glass (Corning HPFS). Substrate temperature was maintained at 250 _C during the deposition. Thickness and deposition rate were controlled with a thickness measuring system Inficon XTC/2. The experimental results of the optical measurements carried out during and after the deposition process have been presented. Physical thickness measurements were made during the deposition process and resulted in 44 nm/52 nm for Al2O3/MgF2 and 44 nm/50 nm for Al2O3/SiO2 system. Optimization was carried out for ultraviolet region with minimum of reflectance at 300 nm. The influence of post deposition annealing on the crystal structure was determined by X-ray measurements. In the range from ultraviolet to the beginning of visible region, the reflectance of both systems decreased and reached minimum at 290 nm. The value of reflectance at this point, for the coating Al2O3/MgF2 was equal to R290nm = 0.6 % and for Al2O3/SiO2R290nm = 1.1 %. Despite the difference between these values both are sufficient for applications in the UV optical systems for medicine and UV laser technology. </abstract>

Bilayer antireflective coatings consisting of aluminium oxide Al2O3/MgF2 and Al2O3/SiO2 are presented in this paper. Oxide films were deposited by means of e-gun evaporation in vacuum of 5 × 10-3 Pa in the presence of oxygen, and magnesium fluoride was prepared by thermal evaporation on heated optical lenses made from quartz glass (Corning HPFS). Substrate temperature was maintained at 250 _C during the deposition. Thickness and deposition rate were controlled with a thickness measuring system Inficon XTC/2. The experimental results of the optical measurements carried out during and after the deposition process have been presented. Physical thickness measurements were made during the deposition process and resulted in 44 nm/52 nm for Al2O3/MgF2 and 44 nm/50 nm for Al2O3/SiO2 system. Optimization was carried out for ultraviolet region with minimum of reflectance at 300 nm. The influence of post deposition annealing on the crystal structure was determined by X-ray measurements. In the range from ultraviolet to the beginning of visible region, the reflectance of both systems decreased and reached minimum at 290 nm. The value of reflectance at this point, for the coating Al2O3/MgF2 was equal to R290nm = 0.6 % and for Al2O3/SiO2R290nm = 1.1 %. Despite the difference between these values both are sufficient for applications in the UV optical systems for medicine and UV laser technology.

Antireflective bilayer coatings based on Al2O3 film for UV region

AGH – University of Science and Technology, al. Mickiewicza 30, 30-059 Krakow, Poland

PEVIN, ul. Piaskowa 55, 31-341 Krakow, Poland

The Henryk Niewodniczanski Institute of Nuclear Physics PAN, ul. Radzikowskiego 152, 31-342 Krakow, Poland

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Antireflective bilayer coatings based on AlO film for UV region

Bilayer antireflective coatings consisting of aluminium oxide Al2O3/MgF2 and Al2O3/SiO2 are presented in this paper. Oxide films were deposited by means of...

Antireflective bilayer coatings based on Al₂O₃ film for UV region

Publié en ligne: 13 mars 2015

Pages: 6 - 10

Reçu: 13 janv. 2014

Accepté: 14 oct. 2014

DOI: https://doi.org/10.1515/msp-2015-0011

© 2015

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.