<abstract xmlns="http://www.w3.org/1999/xhtml">(La, Nd)2/3TiO3 ceramics were prepared through a conventional solid state mixed oxide route. For phase and microstructure analysis, XRD and SEM were used, respectively. Microwave dielectric properties were measured using a network analyzer. XRD patterns revealed the formation of the parent (La, Nd)2/3TiO3 phase along with (La, Nd)4Ti9O24 as a secondary phase. The microstructure consisted of rectangular and needle shaped grains, which decreased in size from 4 μm to 2 μm with an increase in sintering temperature from 1300 °C to 1350 °C. Decrease in grain size caused an increase in density of the samples from 4.81 g/cm3 to 5.17 g/cm3. Microwave dielectric properties of the samples calcined and sintered in air atmosphere were εr = 40.35, Q × f = 3499 GHz and τf = 0 ppm/°C, whereas for a sample calcined in nitrogen and sintered in air they were εr = 40.18, Q × f = 4077 GHz and τf = +4.9 ppm/°C, respectively. </abstract>

(La, Nd)2/3TiO3 ceramics were prepared through a conventional solid state mixed oxide route. For phase and microstructure analysis, XRD and SEM were used, respectively. Microwave dielectric properties were measured using a network analyzer. XRD patterns revealed the formation of the parent (La, Nd)2/3TiO3 phase along with (La, Nd)4Ti9O24 as a secondary phase. The microstructure consisted of rectangular and needle shaped grains, which decreased in size from 4 μm to 2 μm with an increase in sintering temperature from 1300 °C to 1350 °C. Decrease in grain size caused an increase in density of the samples from 4.81 g/cm3 to 5.17 g/cm3. Microwave dielectric properties of the samples calcined and sintered in air atmosphere were εr = 40.35, Q × f = 3499 GHz and τf = 0 ppm/°C, whereas for a sample calcined in nitrogen and sintered in air they were εr = 40.18, Q × f = 4077 GHz and τf = +4.9 ppm/°C, respectively.

Phase, microstructure and microwave dielectric properties of A-site deficient (La, Nd)2/3TiO3 perovskite ceramics

Materials Research Laboratory, Institute of Physics and Electronics, University of Peshawar, 25120, Pakistan

School of Earth and Space Sciences, Peking University, Beijing 100871, China

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Phase, microstructure and microwave dielectric properties of A-site deficient (La, Nd)TiO perovskite ceramics

(La, Nd)2/3TiO3 ceramics were prepared through a conventional solid state mixed oxide route. For phase and microstructure analysis, XRD and SEM were used,...

Phase, microstructure and microwave dielectric properties of A-site deficient (La, Nd)_2/3TiO₃ perovskite ceramics

Publié en ligne: 13 mars 2015

Pages: 126 - 130

Reçu: 07 août 2014

Accepté: 30 sept. 2014

DOI: https://doi.org/10.1515/msp-2015-0005

© 2015

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.