<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>In this work preparation and characteristic of modified nanocarbons is described. These materials were obtained using nanocrystalline iron as a catalyst and ethylene as a carbon source at 700°C. The influence of argon or hydrogen addition to reaction mixture was investigated. After ethylene decomposition samples were hydrogenated at 500°C. As a results iron carbide (Fe<sub>3</sub>C) in the carbon matrix in the form of multi walled carbon nanotubes was obtained. After a treatment under hydrogen atmosphere iron carbide decomposed to iron and carbon and small iron particles agglomerated into larger ones.</p></abstract>

In this work preparation and characteristic of modified nanocarbons is described. These materials were obtained using nanocrystalline iron as a catalyst and ethylene as a carbon source at 700°C. The influence of argon or hydrogen addition to reaction mixture was investigated. After ethylene decomposition samples were hydrogenated at 500°C. As a results iron carbide (Fe3C) in the carbon matrix in the form of multi walled carbon nanotubes was obtained. After a treatment under hydrogen atmosphere iron carbide decomposed to iron and carbon and small iron particles agglomerated into larger ones.

Preparation of carbon nanotubes using cvd CVD method

Institute of Chemical and Environment Engineering, West Pomeranian University of Technology, ul. Pułaskiego 10, 70-322 Szczecin, Poland

Polish Journal of Chemical Technology

{"article-title":"Preparation of carbon nanotubes using cvd CVD method"}

In this work preparation and characteristic of modified nanocarbons is described. These materials were obtained using nanocrystalline iron as a catalyst and...

Preparation of carbon nanotubes using cvd CVD method

Publicado en línea: 27 sept 2010

Páginas: 45 - 49

DOI: https://doi.org/10.2478/v10026-010-0033-y

Palabras clave
iron catalyst, carbon nanomaterials, ethylene decomposition, hydrogenation

This content is open access.

Preparation of carbon nanotubes using cvd CVD method

Publicado en línea: 27 sept 2010

Páginas: 45 - 49

DOI: https://doi.org/10.2478/v10026-010-0033-y

Palabras claveiron catalyst, carbon nanomaterials, ethylene decomposition, hydrogenation

This content is open access.

Palabras clave
iron catalyst, carbon nanomaterials, ethylene decomposition, hydrogenation