<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>In this paper a review of the recent studies on the synthesis of zeolites from expanded perlite under hydrothermal conditions is presented. Attention is paid to possible outcomes of synthesis from low cost glass material, such as perlite. The study also investigates the phase composition of zeolitic materials obtained by modification of by-product derived from an expanded perlite production process. The synthesis was made using the hydrothermal method with sodium hydroxide under autogenous pressure at a temperature below 100 °C for 1 to 72 h. It was possible to obtain a zeolitic material at a temperature as low as 60 °C using 4.0 M NaOH. The X-ray diffraction pattern showed the biggest peak intensity of zeolite X with 4.0 M NaOH at the temperature of 70 °C. During synthesis at higher temperature zeolite Na-P1 (with 3.0 M NaOH at 90 °C) and hydroxysodalite (with 5.0 M NaOH at 90 °C) were obtained.</p></abstract>

In this paper a review of the recent studies on the synthesis of zeolites from expanded perlite under hydrothermal conditions is presented. Attention is paid to possible outcomes of synthesis from low cost glass material, such as perlite. The study also investigates the phase composition of zeolitic materials obtained by modification of by-product derived from an expanded perlite production process. The synthesis was made using the hydrothermal method with sodium hydroxide under autogenous pressure at a temperature below 100 °C for 1 to 72 h. It was possible to obtain a zeolitic material at a temperature as low as 60 °C using 4.0 M NaOH. The X-ray diffraction pattern showed the biggest peak intensity of zeolite X with 4.0 M NaOH at the temperature of 70 °C. During synthesis at higher temperature zeolite Na-P1 (with 3.0 M NaOH at 90 °C) and hydroxysodalite (with 5.0 M NaOH at 90 °C) were obtained.

Low-temperature synthesis of zeolite from perlite waste — Part I: review of methods and phase compositions of resulting products

Faculty of Materials Science and Ceramic, AGH University of Science and Technology, 30 Mickiewicza Av., 30-059, Krakow, Poland

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

In this paper a review of the recent studies on the synthesis of zeolites from expanded perlite under hydrothermal conditions is presented. Attention is paid...

Low-temperature synthesis of zeolite from perlite waste — Part I: review of methods and phase compositions of resulting products

Publicado en línea: 17 oct 2014

Páginas: 503 - 513

DOI: https://doi.org/10.2478/s13536-014-0216-y

Palabras clave
synthesis of zeolites, zeolite X, expanded perlite waste, FT-IR spectra

© 2014 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Low-temperature synthesis of zeolite from perlite waste — Part I: review of methods and phase compositions of resulting products

Publicado en línea: 17 oct 2014

Páginas: 503 - 513

DOI: https://doi.org/10.2478/s13536-014-0216-y

Palabras clavesynthesis of zeolites, zeolite X, expanded perlite waste, FT-IR spectra

© 2014 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
synthesis of zeolites, zeolite X, expanded perlite waste, FT-IR spectra