<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>The aim of this work was to prepare BiFeO3 by modified solid-state sintering and mechanical activation processes and to investigate the structure and hyperfine interactions of the material. X-ray diffraction and Mössbauer spectroscopy were applied as complementary methods. In the case of sintering, BiFeO3 phase was obtained from the mixture of precursors with 3 and 5 % excess of Bi2O3 during heating at 1023 K. Small amounts of impurities such as Bi2Fe4O9 and sillenite were recognized. In the case of mechanical activation, the milling of stoichiometric amounts of Bi2O3 and Fe2O3 followed by isothermal annealing at 973 K resulted in formation of the mixture of BiFeO3, Bi2Fe4O9, sillenite and hematite. After separate milling of individual Bi2O3 and Fe2O3 powders, mixing, further milling and thermal processing, the amount of desired BiFeO3 pure phase was significantly increased (from 70 to 90 %, as roughly estimated). From Mössbauer spectra, the hyperfine interaction parameters of the desired BiFeO3 compound, paramagnetic impurities of Bi2Fe4O9 and sillenite were determined. The main conclusion is that the lowest amount of impurities was obtained for BiFeO3 with 3 % excess of Bi2O3, which was sintered at 1023 K. However, in the case of mechanical activation, the pure phase formed at a temperature by 50 K lower as compared to solid-state sintering temperature. X-ray diffraction and Mössbauer spectroscopy revealed that for both sintered and mechanically activated BiFeO3 compounds, thermal treatment at elevated temperature led to a partial eliminating of the paramagnetic impurities.</p></abstract>

The aim of this work was to prepare BiFeO3 by modified solid-state sintering and mechanical activation processes and to investigate the structure and hyperfine interactions of the material. X-ray diffraction and Mössbauer spectroscopy were applied as complementary methods. In the case of sintering, BiFeO3 phase was obtained from the mixture of precursors with 3 and 5 % excess of Bi2O3 during heating at 1023 K. Small amounts of impurities such as Bi2Fe4O9 and sillenite were recognized. In the case of mechanical activation, the milling of stoichiometric amounts of Bi2O3 and Fe2O3 followed by isothermal annealing at 973 K resulted in formation of the mixture of BiFeO3, Bi2Fe4O9, sillenite and hematite. After separate milling of individual Bi2O3 and Fe2O3 powders, mixing, further milling and thermal processing, the amount of desired BiFeO3 pure phase was significantly increased (from 70 to 90 %, as roughly estimated). From Mössbauer spectra, the hyperfine interaction parameters of the desired BiFeO3 compound, paramagnetic impurities of Bi2Fe4O9 and sillenite were determined. The main conclusion is that the lowest amount of impurities was obtained for BiFeO3 with 3 % excess of Bi2O3, which was sintered at 1023 K. However, in the case of mechanical activation, the pure phase formed at a temperature by 50 K lower as compared to solid-state sintering temperature. X-ray diffraction and Mössbauer spectroscopy revealed that for both sintered and mechanically activated BiFeO3 compounds, thermal treatment at elevated temperature led to a partial eliminating of the paramagnetic impurities.

Comparative X-ray diffraction and Mössbauer spectroscopy studies of BiFeO3 ceramics prepared by conventional solid-state reaction and mechanical activation

Institute of Electronics and Information Technology, Faculty of Electrical Engineering and Computer Science, Lublin University of Technology, Nadbystrzycka str. 38A, PL-20-618, Lublin, Poland

Department of Materials Science, University of Silesia, Śnieżna str. 2, PL-41-200, Sosnowiec, Poland

Faculty of Materials Science and Engineering, Warsaw University of Technology, Wołoska str. 141, PL-02-507, Warsaw, Poland

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The aim of this work was to prepare BiFeO3 by modified solid-state sintering and mechanical activation processes and to investigate the structure and hyperfine...

Comparative X-ray diffraction and Mössbauer spectroscopy studies of BiFeO3 ceramics prepared by conventional solid-state reaction and mechanical activation

Publicado en línea: 20 abr 2013

Páginas: 211 - 220

DOI: https://doi.org/10.2478/s13536-012-0093-1

Palabras clave
bismuth ferrite, ceramics, sintering, mechanical activation, Mössbauer spectroscopy

© 2013 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Comparative X-ray diffraction and Mössbauer spectroscopy studies of BiFeO3 ceramics prepared by conventional solid-state reaction and mechanical activation

Publicado en línea: 20 abr 2013

Páginas: 211 - 220

DOI: https://doi.org/10.2478/s13536-012-0093-1

Palabras clavebismuth ferrite, ceramics, sintering, mechanical activation, Mössbauer spectroscopy

© 2013 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
bismuth ferrite, ceramics, sintering, mechanical activation, Mössbauer spectroscopy