<p>Post-cast application of hydrophobic agents onto hardened concrete is successful at reducing external ion diffusion into cement paste, this work examines pre-cast application of hydrophobic admixtures in fresh concrete. Concretes, with water to cement ratios (w/c) 0.45 and 0.50 (CEM I; low C3A), were mixed. Adding alkyltrialkoxysilane or triacylglycerol admixtures ranging from 1 to 3 wt%cem in these concretes were evaluated. Increasing the dosage of hydrophobic admixtures decreased the compressive strength. The usage of these admixtures did not hinder the further development of the microstructure as all concretes gained strength after one year, but not in the same percentage increase as the reference concrete. Chloride ion diffusion, after exposure to 3 wt% NaCl solution at 20 °C for 91 days, in concretes with 1 wt%cem admixture showed slight reductions in diffusion rate (8-17%) compared to the reference. At 3 wt%cem, triacylglycerol admixtures showed better hindering effects of inward chloride diffusion, this was especially evident in w/c = 0.45. Equivalent addition of alkyltrialkoxysilane-based admixtures increased the diffusion of chloride ions transferred into the cement matrix.</p>
</abstract>

Post-cast application of hydrophobic agents onto hardened concrete is successful at reducing external ion diffusion into cement paste, this work examines pre-cast application of hydrophobic admixtures in fresh concrete. Concretes, with water to cement ratios (w/c) 0.45 and 0.50 (CEM I; low C3A), were mixed. Adding alkyltrialkoxysilane or triacylglycerol admixtures ranging from 1 to 3 wt%cem in these concretes were evaluated. Increasing the dosage of hydrophobic admixtures decreased the compressive strength. The usage of these admixtures did not hinder the further development of the microstructure as all concretes gained strength after one year, but not in the same percentage increase as the reference concrete. Chloride ion diffusion, after exposure to 3 wt% NaCl solution at 20 °C for 91 days, in concretes with 1 wt%cem admixture showed slight reductions in diffusion rate (8-17%) compared to the reference. At 3 wt%cem, triacylglycerol admixtures showed better hindering effects of inward chloride diffusion, this was especially evident in w/c = 0.45. Equivalent addition of alkyltrialkoxysilane-based admixtures increased the diffusion of chloride ions transferred into the cement matrix.

Chloride Ion Diffusion Resistance of Bulk Hydrophobic Concrete: Comparison of w/c and Dosages

Dept. of Civil & Architectural Engineering

PhD, Department Manager, Havsfiskelaboratoriet / SLU-Aqua

Nordic Concrete Research

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Post-cast application of hydrophobic agents onto hardened concrete is successful at reducing external ion diffusion into cement paste, this work examines...

Chloride Ion Diffusion Resistance of Bulk Hydrophobic Concrete: Comparison of w/c and Dosages

Publicado en línea: 22 jul 2023

Páginas: 17 - 38

Recibido: 31 dic 2022

Aceptado: 18 abr 2023

DOI: https://doi.org/10.2478/ncr-2022-0020

Palabras clave
Admixtures, alkyl trialkoxysilanes, chloride diffusion, concrete, hydrophobic, silane, triacylglycerol, vegetable oil

© 2023 Patrick Rogers et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Chloride Ion Diffusion Resistance of Bulk Hydrophobic Concrete: Comparison of w/c and Dosages

Publicado en línea: 22 jul 2023

Páginas: 17 - 38

Recibido: 31 dic 2022

Aceptado: 18 abr 2023

DOI: https://doi.org/10.2478/ncr-2022-0020

Palabras claveAdmixtures, alkyl trialkoxysilanes, chloride diffusion, concrete, hydrophobic, silane, triacylglycerol, vegetable oil

© 2023 Patrick Rogers et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
Admixtures, alkyl trialkoxysilanes, chloride diffusion, concrete, hydrophobic, silane, triacylglycerol, vegetable oil