Synthesis of thermochromic VO2 (M) was successfully done by annealing hydrothermally-prepared VO2 (B) at different temperatures and times. Conversion of the metastable VO2 (B) to the thermochromic VO2 polymorph was studied using thermogravimetric analyzer (TGA) under N2 atmosphere. Moreover, the phase and morphology of the synthesized samples were studied using X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM), respectively. Accordingly, the XRD scans of all the annealed samples exhibited the presence of monoclinic VO2 (M), while the FE-SEM images of the samples showed the formation of nanorods and nanospheres, particularly those heated at high temperatures (650 °C and 700 °C). Meanwhile, differential scanning calorimetry (DSC) was used to measure the phase transition temperature (τc), hysteresis, and enthalpy of the prepared VO2. Based on these results, all samples displayed a τc of about 66 °C. However, the hysteresis was high for the samples annealed at lower temperatures (550 °C and 600 °C), while the enthalpy was very low for samples heated at lower annealing time (1.5 h and 1 h). These findings showed that crystallinity and nanostructure formation affected the thermochromic properties of the samples. In particular, the sample annealed at 650 °C showed better crystallinity and improved thermochromic behavior.
</abstract>

Synthesis of thermochromic VO2 (M) was successfully done by annealing hydrothermally-prepared VO2 (B) at different temperatures and times. Conversion of the metastable VO2 (B) to the thermochromic VO2 polymorph was studied using thermogravimetric analyzer (TGA) under N2 atmosphere. Moreover, the phase and morphology of the synthesized samples were studied using X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM), respectively. Accordingly, the XRD scans of all the annealed samples exhibited the presence of monoclinic VO2 (M), while the FE-SEM images of the samples showed the formation of nanorods and nanospheres, particularly those heated at high temperatures (650 °C and 700 °C). Meanwhile, differential scanning calorimetry (DSC) was used to measure the phase transition temperature (τc), hysteresis, and enthalpy of the prepared VO2. Based on these results, all samples displayed a τc of about 66 °C. However, the hysteresis was high for the samples annealed at lower temperatures (550 °C and 600 °C), while the enthalpy was very low for samples heated at lower annealing time (1.5 h and 1 h). These findings showed that crystallinity and nanostructure formation affected the thermochromic properties of the samples. In particular, the sample annealed at 650 °C showed better crystallinity and improved thermochromic behavior.

Effects of annealing parameters on phase, structure and thermochromic properties of VO2 (M) derived from nanostructured VO2(B)

Department of Physics, Faculty of Science

Mindanao State University – Main Campus

Department of Chemistry, Faculty of Science

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Effects of annealing parameters on phase, structure and thermochromic properties of VO (M) derived from nanostructured VO(B)

Synthesis of thermochromic VO2 (M) was successfully done by annealing hydrothermally-prepared VO2 (B) at different temperatures and times. Conversion of the...

Effects of annealing parameters on phase, structure and thermochromic properties of VO₂ (M) derived from nanostructured VO₂(B)

Publicado en línea: 13 abr 2021

Páginas: 661 - 666

Recibido: 29 oct 2018

Aceptado: 23 abr 2019

DOI: https://doi.org/10.2478/msp-2020-0071

Palabras clave
annealing, hydrothermal synthesis, thermochromic, vanadium dioxide

© 2020 Hamdi Muhyuddin Barra et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Effects of annealing parameters on phase, structure and thermochromic properties of VO2 (M) derived from nanostructured VO2(B)

Publicado en línea: 13 abr 2021

Páginas: 661 - 666

Recibido: 29 oct 2018

Aceptado: 23 abr 2019

DOI: https://doi.org/10.2478/msp-2020-0071

Palabras claveannealing, hydrothermal synthesis, thermochromic, vanadium dioxide

© 2020 Hamdi Muhyuddin Barra et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Effects of annealing parameters on phase, structure and thermochromic properties of VO₂ (M) derived from nanostructured VO₂(B)

Palabras clave
annealing, hydrothermal synthesis, thermochromic, vanadium dioxide